Abstract:In order to investigate the effect of heat treatment on the microstructure and tensile properties of an Mg-5Gd-4Y-0.5Zn-0.5Zr alloy, the phase diagram was calculated by Pandat software, and accordingly the as-extruded alloy was annealed at 450, 510 and 550 °C followed by water quenching. The microstructure and mechanical properties of the specimens were analyzed subsequently by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and tensile testing. The results showed that the average grain size of the as-extruded specimen was about 4 μm, in which Mg24Y5 was detected, and fine-grain strip was formed during the extrusion process. The grain size of the specimen annealed at 450 °C for 24 h was about 11 μm, and the main secondary phases were 14H-LPSO, δ-Zr3Zn2, β1-Mg3Gd and (HCP)Zr particles. The plate-like 14H-LPSO and cubic β1- Mg3Gd phases were coherent with the matrix, and the surface layer of (HCP)Zr was enriched with Zn atoms. When the annealing temperature reached 510 °C and 550 °C, the grain size increased to about 83 and 151 μm, respectively. The 14H-LPSO phases were gradually dissolved while the other secondary phases still existed. It was shown by uniaxial tensile testing that the ultimate tensile strength (UTS), yield tensile strength (YTS) and elongation (EL) of the as-extruded specimen were 291 MPa, 236 MPa and 24.7%, respectively. Increase of UTS, EL and decrease of YTS was resulted after annealed at 450 °C. However, both the strength and ductility dropped obviously after annealed at 510 °C and 550 °C. Ductile fracture features were found on the fracture surface of the as-extruded and 450 °C annealed specimens, whereas brittle topology, such as cleavage, was the main feature on the fracture surfaces of the specimens annealed at higher temperatures. Based on the strength analysis, it was concluded that the fine-grain strengthening was more important than solution strengthening and precipitation strengthening in this work.

Effect of Mn and Sc on Microstructures and Mechanical Properties of Mg-9Gd-4Y Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Preparation of high-performance Mg-Gd-Y-Mn-Sc alloy by heat treatment and extrusion

Microstructure evolution, mechanical property response and strengthening mechanism induced by compositional effects in Al–6 Mg alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Effects of Mn, Zr on microstructure and properties of Mg-Gd-Y alloys

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Effect of Mn Modification on Microstructure and Mechanical Properties of Magnesium Alloy with Low Gd Content

Effects of extrusion temperature on microstructure evolution and mechanical properties of heterogeneous Mg−Gd alloy laminates via accumulated extrusion bonding

Effect of heat treatment on microstructure and mechanical properties of Mg-4Y-1.6Nd-1Sm-0.5Zr alloy

The Effect of Gd and Zn Additions on Microstructures and Mechanical Properties of Mg-4sm-3nd-Zr Alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

Effects of Heat Treatment and Plastic Deformation on Structure and Properties of Mg-9al-1.2nd-0.45y-0.7zn Mg Alloy

Effect of Annealing on Microstructure and Tensile Properties of As-Extruded Mg-5Gd-4Y-0.5Zn-0.5Zr Alloy

Effect of Y content on microstructure evolution and tensile properties of Mg-8Li-3Al-2Sn-xY alloys

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys