Engineering of Interconnected Ionic Channels in Polybenzimidazole Anion-Exchange Membranes

Ruizhen Yang,Xuemei Wu,Wanting Chen,Xiaozhou Wang,Tiantian Li,Xiaoming Yan,Leilei Wang,Fujun Cui,Gaohong He
DOI: https://doi.org/10.1021/acs.iecr.3c02220
2023-01-01
Industrial & Engineering Chemistry Research
Abstract:To balance the ion conduction and stability of anion-exchange membranes (AEMs), the efficiency of OH- transfer needs to be improved. Here a series of polybenzimidazole-based AEMs (UTA-PBI-x) with comb-shaped tricationic side chains containing two diethoxy spacers and one alkyl spacer were synthesized. It is found that in the low-IEC region, hydrogen-bond network is the dominant contribution to ion transport, while the hydrated ionic channels would gradually become more dominant with increasing ionic content. With an optimal IEC of 1.40 mmol/g, OH- ions could rapidly transfer in the desired hydrated cationic clusters and through the thin intercluster ether-containing hydrogen-bond network domains. Meanwhile, the ether domains guarantee a continuous nonionic phase for resisting water swelling. Consequently, the UTA-PBI-1.40 membrane simultaneously possesses a low swelling ratio of 17.2%, sufficient conductivity of 46.9 mS/cm at 20 degrees C, excellent mechanical strength (21.1 MPa), and good alkaline stability (similar to 90% remaining conductivity) in 1 M NaOH for similar to 1400 h. A high efficiency of OH- transport (sigma/IEC similar to 103.2) was achieved, which is superior to those of the recently reported AEMs. In a H-2/O-2 fuel cell, the ultrathin UTA-PBI-1.40 membrane achieves a peak power density of 861.6 mW/cm(2) at 80 degrees C. This work provides a theoretical and experimental guidance for the design of AEMs with high-efficient OH- transfer.
What problem does this paper attempt to address?