Abstract:A series of semi-interpenetrating polymer network anion exchange membranes (semi-IPN AEMs), composed of a quaternized poly(styrene) (PS) copolymer and crosslinked poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) networks, have been designed and fabricated. In this system, quaternized PS served as an anion transport moiety, while crosslinked PPO networks formed by azide–alkyne cycloaddition under an organic base were expected to maintain the mechanical properties and dimensional stability of the resulting semi-IPN AEMs. The semi-IPN AEMs showed improved mechanical properties compared to the control sample prepared by physical blending without crosslinking. It was found that the sIPN-62/30 AEM with an IEC of 1.44 meq. g−1 showed the highest hydroxide conductivity of 37.2 mS cm−1 at 20 °C and a relatively low swelling ratio of 12% at 20 °C in water. Further increasing the fraction of the linear conductive component (sIPN-75/20) led to a dramatic increase of water uptake, which diluted the ion concentration in the AEMs, consequently decreasing the hydroxide conductivity of the membrane (28 mS cm−1 at 20 °C). However, a high mechanical strength and low swelling ratio were observed for sIPN-75/20 samples due to the presence of hydrophobic crosslinked PPO networks. The alkaline stability of the semi-IPN AEMs was evaluated in 1 M NaOH at 80 °C. 59.1%, 86.7% and 74.8% retention in hydroxide conductivity, weight and IEC values were recorded for the sIPN-62/30 AEM respectively after 700 h testing. This result indicated that the crosslinked networks in semi-IPN AEMs can effectively protect the cations from being attacked by hydroxide ions. A single H2/O2 alkaline fuel cell of the sIPN-62/30 membrane demonstrated that a maximum power density of 110.6 mW cm−2 was achieved at a current density of 280 mA cm−2 at 60 °C. Although a loss of 78.3% of its initial performance was observed for the sIPN-62/30 membrane after 30 h alkaline fuel cell durability testing at 100 mA cm−2, high retention in IEC values and hydroxide conductivity for the aged sIPN-62/30 membrane shows that the semi-IPN AEMs based on BTMA cations are chemically stable under fuel cell operation conditions.

Semi-interpenetrating anion exchange membranes using hydrophobic microporous linear poly(ether ketone)

Poly(olefin)-Based Anion Exchange Membranes Prepared Using Ziegler–Natta Polymerization

Semi-interpenetrating polymer networks by azide–alkyne cycloaddition as novel anion exchange membranes

A High-Performance Anion Exchange Membrane Based on Poly(arylene Ether Sulfone) with a High Concentration of Quaternization Units

Novel Composite Anion Exchange Membranes Based on Quaternized Polyepichlorohydrin for Electromembrane Application

Anion Exchange Membranes Derived from Poly(ionic Liquid) of Poly(bis-Piperidinium) and Polybenzimidazole Blends

Mechanically robust semi-interpenetrating polymer network via thiol-ene chemistry with enhanced conductivity for anion exchange membranes

Poly (biphenyl-isatin-piperidine) anion exchange membrane with high hydroxide conductivity based on hydrophilic alkoxy spacer chains

Semi-interpenetrating network anion exchange membranes based on flexible polystyrene-b-poly(ethylene-co-butylene)-b-polystyrene and rigid Poly(vinylbenzyl chloride) for fuel cell applications

Anion Exchange Membranes with a Semi-Interpenetrating Polymer Network Using 1,6-Dibromohexane As Bifunctional Crosslinker

Anion Exchange Membranes Based on Poly(aryl Piperidinium) Containing Both Hydrophilic and Hydrophobic Side Chains

Construction of Crosslinked Polybenz Imidazole-Based Anion Exchange Membranes with Ether-Bond-free Backbone

Poly(biphenyl Piperidine) Anion Exchange Membranes with Long Hydrophilic Side Chains for Water Electrolysis

Novel Anion Exchange Membranes Based on Quaternized Diblock Copolystyrene Containing a Fluorinated Hydrophobic Block

Highly Ion-Conductive and Alkaline Stable Anion Exchange Membranes Containing Bulky Aryl Units and Symmetric Bis-Piperidinium Branches

Highly Conductive Anion Exchange Membranes with Long Flexible Multication Spacer

Anion Exchange Membranes Based on Sulfonated Poly(ether ether ketone) Crosslinked Methylpyrrolidinium Functionalized Poly (vinyl benzyl chloride) with High Chemical Stability

Piperidinium-Functionalized Poly(Vinylbenzyl Chloride) Cross-linked by Polybenzimidazole As an Anion Exchange Membrane with a Continuous Ionic Transport Pathway

Anion Conductive Piperidinium Based Poly (ether Sulfone): Synthesis, Properties and Cell Performance

Mechanically Robust and Highly Conductive Semi-Interpenetrating Network Anion Exchange Membranes for Fuel Cell Applications

Highly conductive fluorinated poly(biphenyl piperidinium) anion exchange membranes with robust durability