Abstract:A series of semi-interpenetrating polymer network anion exchange membranes (semi-IPN AEMs), composed of a quaternized poly(styrene) (PS) copolymer and crosslinked poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) networks, have been designed and fabricated. In this system, quaternized PS served as an anion transport moiety, while crosslinked PPO networks formed by azide–alkyne cycloaddition under an organic base were expected to maintain the mechanical properties and dimensional stability of the resulting semi-IPN AEMs. The semi-IPN AEMs showed improved mechanical properties compared to the control sample prepared by physical blending without crosslinking. It was found that the sIPN-62/30 AEM with an IEC of 1.44 meq. g−1 showed the highest hydroxide conductivity of 37.2 mS cm−1 at 20 °C and a relatively low swelling ratio of 12% at 20 °C in water. Further increasing the fraction of the linear conductive component (sIPN-75/20) led to a dramatic increase of water uptake, which diluted the ion concentration in the AEMs, consequently decreasing the hydroxide conductivity of the membrane (28 mS cm−1 at 20 °C). However, a high mechanical strength and low swelling ratio were observed for sIPN-75/20 samples due to the presence of hydrophobic crosslinked PPO networks. The alkaline stability of the semi-IPN AEMs was evaluated in 1 M NaOH at 80 °C. 59.1%, 86.7% and 74.8% retention in hydroxide conductivity, weight and IEC values were recorded for the sIPN-62/30 AEM respectively after 700 h testing. This result indicated that the crosslinked networks in semi-IPN AEMs can effectively protect the cations from being attacked by hydroxide ions. A single H2/O2 alkaline fuel cell of the sIPN-62/30 membrane demonstrated that a maximum power density of 110.6 mW cm−2 was achieved at a current density of 280 mA cm−2 at 60 °C. Although a loss of 78.3% of its initial performance was observed for the sIPN-62/30 membrane after 30 h alkaline fuel cell durability testing at 100 mA cm−2, high retention in IEC values and hydroxide conductivity for the aged sIPN-62/30 membrane shows that the semi-IPN AEMs based on BTMA cations are chemically stable under fuel cell operation conditions.

Semi-interpenetrating network anion exchange membranes based on quaternized polyvinyl alcohol/poly(diallyldimethylammonium chloride)

Facile Preparation of Novel Cardo Poly(oxindolebiphenylylene) with Pendent Quaternary Ammonium by Superacid-Catalysed Polyhydroxyalkylation Reaction for Anion Exchange Membranes

Facile Fabrication of Poly(vinyl Alcohol)/polyquaternium‐10 (PVA/PQ‐10) Anion Exchange Membrane with Semi‐Interpenetrating Network

Novel Composite Anion Exchange Membranes Based on Quaternized Polyepichlorohydrin for Electromembrane Application

Diamine Crossklinked Anion Exchange Membranes Based on Poly(vinyl Benzyl Methylpyrrolidinium)

Highly Alkaline Stable Fully-Interpenetrating Network Poly(styrene-Co-4-vinyl Pyridine)/polyquaternium-10 Anion Exchange Membrane Without Aryl Ether Linkages

Synthesis and characterization of long-side-chain type quaternary ammonium-functionalized poly (ether ether ketone) anion exchange membranes

A High-Performance Anion Exchange Membrane Based on Poly(arylene Ether Sulfone) with a High Concentration of Quaternization Units

Semi-interpenetrating anion exchange membranes using hydrophobic microporous linear poly(ether ketone)

Alkali Resistant Cross-Linked Poly(Arylene Ether Sulfone)S Membranes Containing Aromatic Side-Chain Quaternary Ammonium Groups

Semi-interpenetrating polymer networks by azide–alkyne cycloaddition as novel anion exchange membranes

Anion Exchange Membranes with a Semi-Interpenetrating Polymer Network Using 1,6-Dibromohexane As Bifunctional Crosslinker

Poly(phenylene Oxide)-Based Anion Exchange Membranes Having Linear Cross-Linkers or Star Cross-Linkers

Novel Anion Exchange Membranes Based on Quaternized Diblock Copolystyrene Containing a Fluorinated Hydrophobic Block

Azide-Assisted Self-Crosslinking of Highly Ion Conductive Anion Exchange Membranes

Alkali-resistant poly (vinyl benzyl chloride) based anion exchange membranes with outstanding flexibility and high hydroxide ion conductivity

Anion Exchange Membrane with a Novel Quaternized Ammonium Containing Long Ether Substituent

Alkali Resistant Anion Exchange Membranes Based on Saturated Heterocyclic Quaternary Ammonium Cations Functionalized Poly(2,6-dimethyl-1,4-phenylene oxide)s

Hydrophilic Flexible Ether Containing, Cross-Linked Anion Exchange Membrane Quaternized with DABCO.

Different cationic functionalized epichlorohydrin modified polyvinyl alcohol based anion exchange membrane

Improving the Conductivity and Dimensional Stability of Anion Exchange Membranes by Grafting of Quaternized Dendrons