Coordination Driven Vanadium/l-Cysteine Hybrid Conversion Film to Improve the Corrosion Resistance of Copper

Chunchao Chen,Xiang Gao,Kanglu Feng,Juan Qiu,Kangwei Gongsun,Changming Bu,Zhandong Chi,Houyi Ma
DOI: https://doi.org/10.1016/j.surfcoat.2023.130170
2023-01-01
Abstract:Vanadium/L-cysteine (V/L-cys) hybrid films with favorable anti-corrosion performance were fabricated on copper substrate based on the coordination between Vanadium and L-cys. The characteristic adsorption of sulfhydryl groups (-SH) in L-cys on copper acts as a bridge for film formation, while the coordination between VO2+ ions and -COOH or NH2 in L-cys repairs defects and enhances the density of film. The EIS results indicated that the corrosion protection efficiency of V/L-cys film was 99.6 %, which was much higher than that of single Lcys film (91.1 %). Moreover, the immersion test exhibited that V/L-cys film was capable of enduring 300 min of immersion in a 3.5 % NaCl solution, whereas L-cys film could only withstand 60 min of immersion. The durability of V/L-cys film showed a significantly higher level than that of L-cys film.
What problem does this paper attempt to address?