Abstract:Aluminum alloys are extensively used to manufacture mechanical components. However, when exposed to alkaline environments, like lubricants, refrigerants, or detergents, they can be corroded, reducing their durability. For this reason, the aim of this study is to investigate the influence of aggressive alkaline solutions (i.e., pH and presence of chlorides) on the corrosion resistance of three aluminum alloys (AA 5083-H111, AA 6082-T6, and AA 7075-T6) with and without anodizing treatments. Open circuit potential (EOCP) and anodic polarization measurements were carried out and typical corrosion parameters such as corrosion current density (icor) and corrosion rate (CR) were determined. Morphology of the corrosion attack and samples microstructure were investigated by scanning electron microscope. Results show that corrosion behavior of the three investigated alloys is influenced by (i) the aggressiveness of the testing environments; (ii) the thickness of the anodizing treatment; (iii) the alloy chemical composition; (iv) the distribution of intermetallic phases in the aluminum matrix. Moreover, three galvanic series have been built also testing other metallic alloys commonly used in mechanical applications, i.e., carbon steel (C40), stainless-steel (AISI 304), and Cu-based alloys (Cu-Ni alloy and CW 617 N, respectively). Results clearly indicate that galvanic series play a fundamental role when it is necessary to select an alloy for a specific environment, highlighting the thermodynamic conditions for corrosion occurrence. On the other hand, kinetic measurements and microstructural studies carried out on the three aluminum alloys stress the importance of the surface treatments and relevant thickness as well as the effect of metal exposure. Future work will involve the study of other surface treatments on aluminum alloys and the evaluation of their corrosion behavior in acidic environments.

Correlation Study of Accelerated Corrosion Testing and Outfield Testing of Aluminum Alloy

Accelerated Corrosion Test on LY12 Aluminum Alloy in Simulated Marine Atmosphere

Investigation of Long-term Corrosion of AA2024 and AA5119 Aluminum Alloys under chromate coating in Marine Atmosphere by Electrochemical Impedance Technology

Study on the Correlation Between Indoor Accelerated Corrosion Testing of Concrete Epoxy Polysiloxane Coating and Real-Sea Environmental Testing in the East China Sea

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Correlation between Laboratory-Accelerated Corrosion and Field Exposure Test for High-Strength Stainless Steels

Atmospheric corrosion acceleration effect on commercial aluminum alloys in current-carrying condition

Predicting Galvanic Corrosion of Aluminum Using Accelerated Laboratory Electrochemical Experiments

Electrochemical Study on Corrosion Damage of 7B04 Aluminum Alloy/Anodic Film/Epoxy Coating System in Simulated Marine Atmospheric Environment

Study on the Effect of Dry and Wet Cycle Time Ratio on the Corrosion Behavior of 2198 Aluminum–Lithium Alloy

Applicability Study on Accelerated Corrosion Methods of Steel Bars in Concrete Structure

Study on a multifactor coupling accelerated test method for anticorrosive coatings in marine atmospheric environments

Study of the role of aluminium and corrosion mechanism in galvalume coating in the marine atmospheric environment

Pitting corrosion of 2A12 aluminum alloy long-scale specimen in simulated seawater splash zone, dynamic waterline zone and full immersion zone

Simulation Investigation on Environment-Induced Pitting Corrosion on the Metal Surface

Corrosion Behavior and Mechanical Performance of 7085 Aluminum Alloy in a Humid and Hot Marine Atmosphere

Corrosion Behavior of High Strength Aluminum Alloy under Different Corrosion Environments

Multi-performance evaluation of high-throughput accelerated corrosion test for high-strength low-alloy 921A steel

Corrosion Behavior of Aluminum Alloys in Different Alkaline Environments: Effect of Alloying Elements and Anodization Treatments

The Effect Spray Testing Condition on the Corrosion Performance of Hydrothermally Sealed Anodic Oxide on a 5005 Aluminum Alloy: Comparison between Neutral Salt Spray, Acetic Salt Spray and Prohesion Testing Methods

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION