Abstract:Purpose In summary, it can be found that the current research on the simulation of natural atmospheric dry–wet alternating accelerated corrosion mainly focused on the study of electrochemical corrosion process and the study of corrosion rate; the micro-pre-corrosion mechanism of materials in this environment, especially for materials. The specific effects of fatigue and fracture performance still lack detailed research. Accordingly, this study aims to more realistically simulate the effect of natural atmospheric corrosion environment on the corrosion resistance and fatigue performance of aircraft skin. Design/methodology/approach In this study, the uniaxial strain control method was used to test the fatigue performance of pre-corrosion samples under simulated natural atmospheric corrosion using MTS809 tensile-torque composite fatigue machine. Scanning electron microscopy, X-ray energy spectrum analysis, atomic force microscopy and X-ray diffraction analysis were used. Fatigue fracture, corrosion morphology and corrosion products were analyzed. Findings The results show that the deep corrosion pit caused by pre-corrosion environment leads to multi-source initiation of crack; the fatigue life of pre-corroded sample decreases by about one-half, chloride ion invades the material and promotes intergranular corrosion; life prediction results show that the natural atmospheric corrosive environment mainly affects the plastic term in the Manson–Coffin formula resulting in a decrease in fatigue life. Originality/value Innovative experimental schemes and materials are used and the test temperature and relative humidity are strictly controlled. The corrosion failure mechanism of 2A70-T6 aluminum alloy under alternating wet and dry accelerated corrosion environment and its influence on fatigue behavior were obtained.

Pitting corrosion of 2A12 aluminum alloy long-scale specimen in simulated seawater splash zone, dynamic waterline zone and full immersion zone

Atmospheric Corrosion Behavior of 2A12 Aluminum Alloy in a Tropical Marine Environment

Influence of Temperature on Initial Corrosion Behavior of Aluminum Alloy 2A12 in Simulated Tank Water Environment

Effects of Exposed Area on Corrosion Behavior of High Strength Aluminum Alloys in Salt Water

Relation between Pitting Corrosion Behavior and Exposed Area of High Strength Aluminum Alloys in Neutral Salt Spray

Mechanistic Studies of Atmospheric Corrosion Behavior of Al and Al-based Alloys in a Tropical Marine Environment

The Relationship of High Strength Aluminum Alloy Corrosion Behavior and Corrosion Environment

Corrosion Behavior of 7A52 Aluminum Alloy Plasma Arc Welding Joint in Simulated Marine Atmosphere Environment

Corrosion and pitting behavior of pure aluminum 1060 exposed to Nansha Islands tropical marine atmosphere

Corrosion Behavior of High Strength Aluminum Alloy under Different Corrosion Environments

Investigation of Long-term Corrosion of AA2024 and AA5119 Aluminum Alloys under chromate coating in Marine Atmosphere by Electrochemical Impedance Technology

Study on the Effect of Dry and Wet Cycle Time Ratio on the Corrosion Behavior of 2198 Aluminum–Lithium Alloy

Electrochemical Corrosion Behavior of Industrial Pure Aluminum in Simulated Seawater

On the localized corrosion of AA5083 in a simulated dynamic seawater/air interface—Part 3: effects of sensitization

Corrosion and Its Micromechanism of Aluminum Casting Alloy in Moist Atmosphere

Corrosion Failure and Mechanical Property Degradation of Anodized 5a06 Aluminum Alloy in a Marine Environment

Atmospheric Corrosion Behaviour of Pure Al 1060 in Tropical Marine Environment

Morphological characteristics and geometric prediction model of pits in complex corrosion environment

Corrosion behavior in aluminum/galvanized steel resistance spot welds and self-piercing riveting joints in salt spray environment

Low-cycle Fatigue Behavior and Corrosion Mechanism of Pre-Corroded 2A70-T6 Aluminum Alloy

Pitting Corrosion of Natural Aged Al–Mg–Si Extrusion Profile