Corrosion Behavior of High Strength Aluminum Alloy under Different Corrosion Environments

ZHOU Song,XU Liang,HUI Li,WANG Lei,MA Shaohua,HAN Fang

DOI: https://doi.org/10.3969/j.issn.1004-132X.2017.16.016

2017-01-01

Abstract:Aiming at the corrosive material problems caused by harsh environment during the service of aviation aluminum alloy materials,research on the corrosion behavior and mechanism of 2xxx aviation aluminum alloys servicing in different corrosive environments(3.5% NaCl solution,wa-ter in fuel tank and wet air)was conducted based on the analyses about the corrosion morphology, openning areas,depths and quantity of the pits,pH values and corrosion products.Results show that corrosion products are mainly found in the first 24 hrs for specimens in 3.5% NaCl solution with the biggest pit depth about 45 μm,with the increase of the corrosion time between 72 ~120 hrs,the in-crease of pit depths and quantities are not obvious.The corrosion behavior for specimens in water in fuel tank was similar to that in NaCl solution,but the pit openning areas and quantities decrease dra-matically.The corrosion extents for specimens in the wet air decrease compaired with the other two corrosive environments with the least pit quantity,the deepest pit depth is lower than 20 μm and the biggest pit openning area is around 5000 μm2 ,the differences among pit depths decrease with the in-crease of corrosion time.