Abstract:In this paper, initiation and growth behavior tests of small fatigue crack in laboratory air and aqueous 3.5% NaCl were conducted using non-corroded and pre-corroded SENT specimens for 2024-T62 Aluminum alloy. In order to compare with the corresponding small cracks, large crack growth tests for non-corroded and corroded specimens with different prior corrosion times were performed. Variation of pre-corrosive pit sizes with corrosion time was also studied. The results show that for fatigue specimens with pre-corrosive pits, small cracks initiated from the corrosion pits in both laboratory air and aqueous 3.5% NaCl, and initiation lives of small cracks (a≤60μm) are below 25% of total fatigue lives. For non-corroded fatigue specimens in laboratory air, small cracks initiated naturally from voids of the material, and initiation lives of small cracks (a≤25μm) are below 20% of total fatigue lives. An obvious small crack effect was found at R=-1 for non-corroded material in laboratory air. However, the same effect was not found at R=0.06 for the non-corroded material in laboratory air, and for the corroded material in both laboratory air and aqueous 3.5% NaCl at R=-1 and 0.06. And effect of environment on growth of small cracks that initiated from pre-corrosive pits was not found for Al2024-T62. The similar tendency was also found in large crack growth tests. Moreover, effect of prior corrosion time on large crack growth rates was not found to be in existence for this material. By assuming a pre-corrosive pit as an initiating surface crack, the commercial software FASTRANII and AFGROW were used to predict fatigue lives of corroded specimens with different prior corrosions. The predictions were found to agree reasonably with the tests.

Corrosion fatigue crack propagation of 7XXX series aluminum alloys from key components of high-speed train

Corrosion fatigue crack propagation behavior of A7N01P‐T4 aluminum alloy welded joints from high‐speed train underframe after 1.8 million km operation

Investigation on corrosion fatigue properties of TA15 alloy in 3.5%NaCl salt spray

Propagation of corrosion induced fatigue crack in aluminum alloy

Corrosion Fatigue Behavior of Fastening Hole Structure and Virtual Crack Propagation Tests

Study on Acoustic Emission Characteristics of Fatigue Damage of A7N01 Aluminum Alloy for High-Speed Trains

Environment-induced Fatigue Cracking Behavior of Aluminum Alloys and Modification Methods

Short Surface Crack Growth of High-Strength Aluminum Alloy in Corrosion Fatigue.

Corrosion fatigue lifetime assessment of high-speed railway axle EA4T steel with artificial scratch

A Study on the Corrosion Fatigue Characteristics of Al 2024-T3 Alloy

Anomalous growth behavior of fatigue crack for the forged 7B04 aluminum alloy

Nanoscale perspective on the stress-corrosion cracking behavior of a peak-aged 7XXX-Al alloy

Small fatigue crack behavior and life prediction of pre-corroded 2024-T62 aluminum alloy

Effect of Fatigue and Precorrosion Fatigue on Fatigue Crack Propagation and Fracture Failure Behavior of 5B70 Aluminum Alloy

Corrosion failure analysis and solutions of aluminum alloy gas path plate used in sanding device of high-speed train

High-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25 CrMo Steel Used in Railway Axle

Stress Corrosion Cracking Behavior of 4.19%Zn-1.34%Mg (A7N01S-T5) Aluminum Alloy Welded Joints

High-Cycle Microscopic Severe Corrosion Fatigue Behavior And Life Prediction Of 25crmo Steel Used In Railway Axles

The Effects of Corrosive Media on Fatigue Performance of Structural Aluminum Alloys

Fatigue Crack Propagation Behavior of the 2195-T8 Aluminum-Lithium Alloy with a Precorroded Hole

Corrosion Fatigue Behavior of 7075 Aluminum Alloy in Saline Water Environment at Different Temperatures