Abstract:A critical determination of a phase diagram of the Zn-Fe binary system was carried out by EPMA analysis for skillfully prepared and equilibrated two-phase alloys for solid phases and by EDS areal analysis for the Fe solubility in the heterogeneously solidified liquid phase instead of the conventional diffusion couple method. It was newly confirmed that equilibrium compositions of intermetallic compounds tend to shift toward the Fe side compared to the previous phase diagram on the whole and that the solubility ranges of the Γ-Fe3Zn10 and Γ1-Fe11Zn40 phases are much narrower than those in the literature. The critical composition of the second-order order-disorder transition between δ1k-FeZn7 and δ1p-FeZn10 at high temperature was estimated by Vickers hardness measurement. Furthermore, the phase separation, i.e., the first-order transition, between the δ1k and δ1p phases in the low temperature region was directly found out and its equilibrium compositions were confirmed by EPMA analysis for the two-phase microstructures. The width of the δ1k + δ1p two-phase region at 500 °C is only 0.5 at.% and the δ1p decomposes into the δ1k and ζ-FeZn13 phases via a eutectoid reaction at a temperature between 455 °C and 445 °C. While being mostly coincident with those in the previous literature at temperatures between 1000 °C and 600 °C, the solubility of Fe in the liquid (L) Zn phase is about twenty times larger than the assessed value in the literature at temperatures below 500 °C. A eutectic reaction, L → ζ + (ηZn), was confirmed to occur by precise EPMA analysis and DSC measurement.

Determination of Isothermal Section of Fe-Ti-Zr Ternary System at 1173 K

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Phase equilibria in Ni–Ti–Ta ternary system

Experimental determination of phase diagram in the Zn-Fe binary system

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Phase equilibria in Co-Ti-Re ternary system

Experimental Investigation and Thermodynamic Assessment of the Mo–Ni–Zr Ternary System

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

Isothermal Section Of Mn-Zr-Si Ternary System At 600 Degrees C

Phase Equilibria of the Ternary Ni-Cr-Zr System and Interfacial Reactions in the Ni-Cr/Zr Couples

Experimental Investigation and Thermodynamic Calculations of the Co-Fe-Ti System

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Experimental determination of the liquidus projection of the B-Cr-Ti system

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C

Experimental determination of isothermal sections for the Co-rich corner of the Co-Cr-Ti system at 800 and 900 °C

The melting diagram of the Ti-corner of the Ti–Zr–Si system and mechanical properties of as-cast compositions