The melting diagram of the Ti-corner of the Ti–Zr–Si system and mechanical properties of as-cast compositions

M. Bulanova,S. Firstov,I. Gornaya,D. Miracle

DOI: https://doi.org/10.1016/j.jallcom.2004.02.060

IF: 6.2

2004-12-01

Journal of Alloys and Compounds

Abstract:Phase equilibria in the Ti-corner of the Ti–Zr–Si system were studied by the methods of metallography, differential thermal analysis, X-ray and microprobe analyses of as-cast samples. The results are given in the way of the melting diagram and of polythermal sections at 10 and 20at.% Si. At 1300°C invariant four-phase equilibrium of eutectic type L↔〈β-Ti〉(β)+〈Ti5Si3〉(Z)+〈(Ti,Zr)2Si〉 (S2) was shown to occur in the concentration interval studied. The location of the eutectic point E was determined to take place at ∼78Ti–11Zr–11Si. The ternary compound S2 formed from the melt by peritectic reaction L+Z→S2. Microhardness of the primary silicide grains and of eutectics microconstituents has shown that zirconium additions decrease the strength of the Z-phase and of the β+Z eutectic, while they do not change the strength of the S2-silicide and of the β+S2 eutectic. Based on the results of hot hardness measurements, below 550°C the potential for attractive high-temperature structural properties is controlled by refinement of the microstructure, while above this temperature the α↔β transformation temperature of Ti limits the application.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering