Abstract:A critical determination of a phase diagram of the Zn-Fe binary system was carried out by EPMA analysis for skillfully prepared and equilibrated two-phase alloys for solid phases and by EDS areal analysis for the Fe solubility in the heterogeneously solidified liquid phase instead of the conventional diffusion couple method. It was newly confirmed that equilibrium compositions of intermetallic compounds tend to shift toward the Fe side compared to the previous phase diagram on the whole and that the solubility ranges of the Γ-Fe3Zn10 and Γ1-Fe11Zn40 phases are much narrower than those in the literature. The critical composition of the second-order order-disorder transition between δ1k-FeZn7 and δ1p-FeZn10 at high temperature was estimated by Vickers hardness measurement. Furthermore, the phase separation, i.e., the first-order transition, between the δ1k and δ1p phases in the low temperature region was directly found out and its equilibrium compositions were confirmed by EPMA analysis for the two-phase microstructures. The width of the δ1k + δ1p two-phase region at 500 °C is only 0.5 at.% and the δ1p decomposes into the δ1k and ζ-FeZn13 phases via a eutectoid reaction at a temperature between 455 °C and 445 °C. While being mostly coincident with those in the previous literature at temperatures between 1000 °C and 600 °C, the solubility of Fe in the liquid (L) Zn phase is about twenty times larger than the assessed value in the literature at temperatures below 500 °C. A eutectic reaction, L → ζ + (ηZn), was confirmed to occur by precise EPMA analysis and DSC measurement.

Experimental determination of phase diagram in the Zn-Fe binary system

Thermodynamic Evaluation of the Fe-Zn Binary System with Reference to the Latest Experimental Phase Diagram

Phase equilibria, crystal structure of δ1-MnZn9 and thermodynamic re-assessment of the Zn-Mn system

Experimental Investigation and Thermodynamic Verification for the Phase Relation around the ε-Mg23 (Al, Zn)30 Intermetallic Compound in the Mg-Zn-Al System

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Experimental determination of the Ni–Ni5Zr eutectic point for binary Ni–Zr alloy phase diagram

Phase equilibrium diagram of the Hf-Fe-Sn system at 1070 K

Phase Equilibria in the Ni-Sn-Zn System at 500°C

Phase Equilibria in the Er-Co, Er-Fe and Er-Co-Fe Systems

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Phase Equilibria of the Binary Ag-In System

Phase diagrams of the Ag-In-Zn ternary system

Thermodynamic calculation of high zinc-containing Al-Zn-Mg-Cu alloy

A Nonconventional Method to Produce Zr Alloys to Study the Fe23Zr6 Intermetallic Compound in the Fe-Zr System

Phase Equilibria of the Sn–Zn–Cu Ternary System

Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents

Experimental Description of the Al-Cu Binary Phase Diagram

Thermodynamic calculation of phase equilibria in the Al–Fe–Zn–O system

New Insights into Solidification and Phase Equilibria in the Al-Al3Zr System: Theoretical and Experimental Investigations

Experimental Investigation and Thermodynamic Assessment of the Mo–Ni–Zr Ternary System