Abstract:Acicular ferrite (AF) has been regarded as the optimal microstructure in steel welds and heat affect zones (HAZs), because of its superior combination of strength and toughness. Although various aspects of AF have been investigated, the crystallographic characteristics of AF, including orientation relationship, variant selection and variant pairing, are still not fully studied. In this research, a Ti-deoxidized high strength low alloy steel was prepared and subjected to HAZ thermal cycle simulation tests to attain AF microstructure. Optical micrographs were obtained and EBSD mappings of AF microstructures were conducted. Through crystallographic analysis, the orientation relationship between AF and austenite was found close to that of bainite transformed at a high temperature (580 °C). In the AF microstructure, all 24 variants are formed and variant selection is nearly random. Compared with bainite, the variant pairing of AF is more random despite the slight favour of certain variant pairs. Most of the adjacent AF laths are from different close-packed plane (CP) groups, leading to the classic interlocking morphology. Meanwhile, a large number of neighbouring AF laths belong to different Bain groups, resulting in a high density of high angle grain boundaries (HAGBs). Intragranular nucleation of primary AF laths on inclusions contributes both to the high HAGB density and to the interlocking morphology of AF, while the sympathetic nucleation of secondary AF laths only contributes to the latter. These results suggest that to increase the HAGB density in AF, promoting the intragranular nucleation on inclusions is more important than enhancing the sympathetic nucleation.

Microstructural Features of a Ultra Low Carbon High Strength Acicular Ferrite Steel Thick Plate

Microstructural Features Of A Ultra Low Carbon High Strength Acicular Ferrite Steel Thick Plate

Toughening Mechanisms of A High-Strength Acicular Ferrite Steel Heavy Plate

Grain refinement mechanism of a 700 MPa ultralow carbon bainite heavy plate steel

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

Variations in microstructure and mechanical properties along thickness direction in a heavy high strength low alloy steel plate

Microstructural Characteristic of Low Carbon Microalloyed Steels Produced by Thermo-Mechanical Controlled Process

Microstructural evolution and grain refinement of a high strength low alloy steel produced by compact strip production

Development of 80 mm Thick Q460 Grade TMCP Plate with High Toughness for Engineering Machinery

Low Density High Strength and High Toughness Steel with Ferrite and Martensite Laminated Structure

MICRO MECHANICAL PROPERTIES AND STABILITY OF ACICULAR FERRITE IN A LOW CARBON MICROALLOYED STEEL

Microstructure and Properties of a Low Carbon Ti-V Microalloyed Steel

Acicular ferrite microstructure in titanium bearing low carbon steels

Coupled Toughening of a Low Carbon Medium Manganese Heavy Steel Plate Investigated by Electron Back–scattered Diffraction (EBSD)

Crystallographic characteristics of acicular ferrite nucleated on inclusions in a HSLA steel

Microstructure and Properties of 1.6%C Ultra-high Carbon Steel

Toughening ultrastrong low-density steel by textured δ-ferrite lamellas

Microstructures and Mechanical Properties of Ferrite-Based Lightweight Steel with Different Compositions

Microstructure and properties of ultrafine grained ultrahigh carbon (1.73 Pct C) steel

Ultrafine Grained Dual-Phase Martensite/ferrite Steel Strengthened and Toughened by Lamella Structure

Microstructural and mechanical properties of ultra-high-strength dual-phase steel produced by ultra-fast cooling