Dominating Role of Film‐Like Carbon‐Enriched Austenite for the Simultaneous Improvement of Strength and Toughness in Low‐Carbon Steel
Kai Yang,Wei Ding,Shilong Liu,Wei Li,Xuejun Jin
DOI: https://doi.org/10.1002/srin.202000344
IF: 2.1258
2020-08-31
steel research international
Abstract:<p>Multiphase microstructures containing film‐like carbon‐enriched austenite as well as martensite matrix, represent an ideal microstructure that can facilitate the break‐through of the trade‐off between strength and toughness, as well as good low‐temperature toughness in high‐strength steels. In this study, to determine the impact of film‐like carbon‐enriched austenite on the toughness of low‐carbon high‐strength steel, quenching and low‐temperature partitioning process was applied to a newly designed alloy. The quenching step resulted in a mixed microstructure consisting of a martensite matrix with high dislocation density and film‐like retained austenite, which was stabilized via carbon enrichment during tempering at 200 ºC for 60 min. Thus, the produced high‐strength steel specimen showed excellent mechanical properties (yield strength = 1201 MPa and tensile strength = 1550 MPa) as well as superior toughness (68.8 J at ‐60 ºC). Its strength primarily resulted from dislocation strengthening, grain boundary strengthening, and solid solution strengthening, and its superior low‐temperature toughness was associated with the film‐like carbon‐enriched austenite, which relaxed local stress, dissipated the plastic energy at the micro‐crack tip, and delayed the initiation and propagation of cracks. Finally, a schematic diagram was designed to elucidate the effect of the retained austenite stabilization on the ductile‐brittle transition temperature.</p><p>This article is protected by copyright. All rights reserved.</p>
metallurgy & metallurgical engineering