Evolution of Ti2Ni Precipitations During Annealing and Their Effects on Properties of Ti–Nb–Ni Foil As PEMFC Bipolar Plates Substrate

Haifeng Zhu,Xiaopeng Wang,Wei Meng,Pingwen Ming,Fantao Kong
DOI: https://doi.org/10.1016/j.ijhydene.2023.01.009
IF: 7.2
2023-01-01
International Journal of Hydrogen Energy
Abstract:In this work, Ti-Nb-Ni foil was cold rolled and different annealing temperatures were conducted. For foils annealed at 600 degrees C, 650 degrees C and 700 degrees C, Ti2Ni particles were evenly distributed in the matrix. Grain growth was obviously confined during annealing at these temperatures. While more (a+Ti2Ni) eutectoids along grain boundaries (GBs) formed in the cases of higher temperatures. Plasticity of as-cold rolled foil was obviously improved by annealing and elongations gradually decreased with annealing temperature. Elongations of foil at 600 degrees C possessed the highest value, viz, 31.6% and 39.8% for RD and TD. For corrosion resistance, 850 degrees C annealed foil had the lowest icorr compared with other counterparts. ICR of as-cold rolled and annealed specimens at 1.4 MPa were all lower than 10 mU cm-2, which satisfied the DOE 2025 target.(c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?