Abstract:In this study, the effect of dual-pulsed gas metal arc welding (DP-GMAW) parameters such as thermal frequency and current amplitude on weldability, microstructural evolution, and mechanical properties of AA7075 alloy joint was investigated. ER53356 filler metal was employed to make AA7075 alloy joints. Thermal frequency in three levels of 1, 2, and 3 Hz was used during the welding process. And current amplitudes of 9, 27, and 45 A were used in three levels as well. After the DP-GMAW process, the welded samples were first checked visually, by a liquid penetrant method, to make sure of their welding soundness. No surface defect or crack was observed. An optical microscope (OM) and a scanning electron microscope (SEM) equipped with energy-dispersive spectroscopy (EDS) were used for microstructural analyses. The hardness of the base metal (BM) and different areas of the welded parts was measured by a microhardness testing method. Results showed that no visual defects were visible on the surface of the joints made under different PD-GMAW variables. As well, microstructural analyses showed that increasing the thermal frequency and current amplitude not only reduced the grain size of the weld metal (WM) and the heat-affected zone (HAZ) but also increased the hardness of these regions. The most refined structure was obtained by employing 2 Hz as frequency and 45 A as current amplitude. The average grain size under these conditions was 71 μm and 52 μm, respectively. It was also observed that increasing the current amplitude had the highest impact in reducing the grain size of the WM. The hardness of the WM and the HAZ, under the optimum frequency, was 91 HVN and 153 HVN, respectively. These values were 85 HVN and 38 HVN under the optimum current amplitude. Moreover, hardness was increased in the HAZ compared with the base metal in all welding conditions. Increasing the thermal frequency not only decreased the distance between the ripples but also increased the number of peak waves created in the fusion line. This was particularly the case in the longitudinal section of the weld and reduced the distance between these waves. On the other hand, increasing the frequency and current amplitude has led to the reduction of porosity in the WM. Finally, increasing the frequency from 1 to 3 Hz led to a 33% reduction in the porosity of the WM. This is while 66% reduction of porosity in the WM was obtained by increasing the current amplitude from 9 to 45 A.

Metal Transfer Behavior in AA6061 Aluminum Alloy Double-Wire Median Pulsed Gas Metal Arc Welding

Dynamic Metal Transfer Behavior in Double-Wire DP-GMAW of Aluminum Alloy Under Different Pulse Phases

Double-Pulse Triple-Wire MIG Welding of 6082-T6 Aluminum Alloy: Process Characteristics and Joint Performances

Influence of Metal Transfer Modes on Pore Formation during the Welding Process of AA6082/A360 Dissimilar Aluminum Alloys

Effect of high-frequency phase shift on metal transfer and weld formation in aluminum alloy double-wire DP-GMAW

Heat input characteristics and weld bead formation in double-wire double-pulsed GMAW of aluminum alloy under different low-frequency phases

Arc characteristic in aluminum alloy double-wire variable polarity double base pulsed gas metal arc welding

Comparative Study of Droplet Transfer Modes on Appearance, Microstructure, and Mechanical Properties of Weld During Pulsed GMAW

Investigation of bypass-coupled double-pulsed directed energy deposition of Al–Mg alloys

The effect of thermal frequency and current amplitude on weldability, microstructural evolution and mechanical properties of AA7075 alloy joint in DP-GMAW process

Solidification Cracking Restraining Mechanism of Al-Cu-Mg-Zn Alloy Welds Using Cold Metal Transfer Technique

Numerical investigation on the influence of current waveform on droplet transfer in pulsed gas metal arc welding

Role of material properties on metal transfer dynamics in gas metal arc welding

Research on Process Characteristics and Properties in Deep-Penetration Variable-Polarity Tungsten Inert Gas Welding of AA7075 Aluminum Alloy

Comparative in Mechanical Behavior of 6061 Aluminum Alloy Welded by Pulsed GMAW with Different Filler Metals and Heat Treatments

Research on Microstructure and Mechanical Properties of Square Wave Alternating Current Tungsten Inert Gas Welded Joints in 2219-T6 Aluminum Alloy

Effect of pulsed metal inert gas (pulsed-MIG) and cold metal transfer (CMT) techniques on hydrogen dissolution in wire arc additive manufacturing (WAAM) of aluminium

Investigation of Droplet Transfer Behaviours in Cold Metal Transfer (CMT) Process on Welding Ti-6Al-4V Alloy

Refined weld microstructure and enhanced joint mechanical property of 1460 Al-Li alloys via double-pulsed variable polarity TIG arc welding

Transient characteristics of ultra-high frequency adjustable multi-pulse gas tungsten welding arc

Investigate the effect of arc characteristic on the mechanical properties of 5A56 Al alloy in CMT arc additive manufacturing