Abstract:In order to improve the anti-ablation property of carbon/carbon (C/C ) composites, ZrC-Cu-C/C composites were fabricated by reactive melt infiltration using C/C composites with the porosity of 38% as preforms and Zr-Cu mixed powders as reactive infiltrators.The effect of infiltrator composition on the ablation resistance of ZrC-Cu-C/C composites was investigated by the test of oxyacetylene flame ablation,and the phase composition and microstructure of the ZrC-Cu-C/C composites before and after ablation were analyzed by XRD,SEM and EDS.The results show that the composites are composed of C,ZrC,Cu and residual Zr before ablation,while there exist C matrix,ZrO2 ,CuO and Cu2 O as well as remnant ZrC and Cu in the surface after ablation for 20 s.Both the linear recession rate and mass loss rate of the composites decrease first and then increase with increasing the content of Zr in infiltrators.The ZrC-Cu-C/C composite fabricated with 60% Zr-Cu(mass fraction)exhibits the best anti-ablation property,whose linear recession rate and mass loss rate are 0.001 8 mm·s-1 and 0.001 3 g·s-1 ,respectively. The ablation mechanisms of the ZrC-Cu-C/C composite are the combination of thermo-physics ablation (based on sublimation of C,melt of ZrO2 and vaporization and sublimation of Cu),thermo-chemical ablation (oxidation of ZrC and C)and mechanical denudation (erosion of the flame).

Ablation Behavior of the ZrC Coating on C/C Composite with the Construction of Thermal Dispersal Network

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Preparation and Ablation Behavior of a ZrB2-SiC Coating-Matrix Integrated C/C Composite

Ablation Behaviors of SiC Nanowire-Reinforced ZrC-SiC Coating-Matrix Integrated C/C Composites with Different Ratios of Precursors

Zrc Ablation Protective Coating for Carbon/Carbon Composites

Microstructure and Ablation Resistance of ZrC Nanostructured Coating for Carbon/carbon Composites

Investigation on Ablation Characteristics of C/C Composites with ZrC/SiC Coating

Ablation Property and Mechanism of ZrC-Cu-C/C Composites

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Microstructures and Ablative Properties of ZrC Coating by Chemical Vapor Deposition

Ablation Behavior of (zrc/sic)3 Alternate Coating Prepared on Sharp Leading Edge C/C Composites by CVD

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Ablation Behavior of ZrC and ZrO2 Coatings on SiC Coated C/C Composites under Oxyacetylene Torch with Different Heat Fluxes

Ablation Resistant Properties And Mechanism Of Zrc Coating Deposited By Plasma-Spraying

Local Anti-Ablation Modification of Uneven-Density C/C Composites with the ZrC-SiC Composite Ceramics

Ablation Resistance of ZrO2-encapsulated ZrB2 Coating with 3D Thermal Conduction Network Applied over Carbon/carbon Composites

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Heat Dissipation of Carbon Shell in ZrC–SiC/TaC Coating to Improve Protective Ability Against Ultrahigh Temperature Ablation

Ablation Behavior of CVD-ZrC Coating under Oxyacetylene Torch Environment with Different Heat Fluxes