Abstract:To date, the most commonly used aluminum alloys for additive manufacturing are eutectic/near-eutectic alloys. However, fabricating high strength aluminum parts has not yet been fully investigated due to solidification cracking and porosity formation, which make these alloys very hard to be processed. Electron beam selective melting (EBSM) of aluminum alloys has some advantages over selective laser melting. The process is not affected by reflectivity of aluminum powders, and parts exhibit less induced thermal stresses. In addition, oxidation is reduced due to vacuum condition. Therefore, the process provides high potential for the fabrication of aluminum alloys, specifically, Al2024 alloy which is widely used in different industries such as automotive and airline industries. Hence, these industries are highly benefitted from being able to build defect-free AM parts. This study is significant because Al2024 alloy is highly susceptible to solidification cracking and porosity formation, and crack-free samples with high relative densities have not been built by EBM process previously. The baseplate preheating temperature was set to 350 degrees C, and samples were fabricated by applying a proper powder bed preheating configuration for each layer. Different sets of processing parameters were used to investigate their effect on the performance of the parts. Archimedes technique was used to measure the relative density of samples, ranging from 95% to full-dense. The results showed that higher relative densities could be achieved by increasing the input energy to an optimum value; however, by further increasing the energy, the relative density decreases, which can be attributed to porosity formation. SEM and EBSD results showed equiaxed grains in a crack-free microstructure. Grain structure consisted of high angle grain boundaries having different crystallographic orientations with a few subgrains. Additionally, AlCuMnFe, AlCuMnFeSi, and eutectic Al2Cu phases were uniformly distributed in the alpha phase matrix. Microhardness results showed an almost uniform change of hardness values in both horizontal and vertical sections, ranging from 100 HV to 110 HV for as-built samples. Moreover, tensile and yield strengths of as-built samples reached 314 MPa and 191 MPa, respectively, which can be further increased by a proper post-processing treatment. (C) 2020 Elsevier B.V. All rights reserved.

Effect of Powder Characteristics on Relative Density and Porosity Formation During Electron Beam Selective Melting of Al2024 Aluminum Alloy

Effect of Processing Parameters on the Densification of an Additively Manufactured 2024 Al Alloy

Selective electron beam melting of high strength Al2024 alloy; microstructural characterization and mechanical properties

Non-Equilibrium Solidification Behavior With Solute Trapping Associated With Powder Characteristics During Electron Beam Additive Manufacturing

Non-equilibrium solidification behavior associated with powder characteristics during electron beam additive manufacturing

Effect of Aluminium Content and Processing Parameters on the Microstructure and Mechanical Properties of Laser Powder-Bed Fused Magnesium-Aluminium (0, 3, 6, 9wt%) Powder Mixture

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Particle Defects and Related Properties of Metallic Powders Produced by Plasma Rotating Electrode Process

Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Effect of Processing Parameters on Forming Defects During Selective Laser Melting of AlSi10Mg Powder

Effects of powders and process parameters on density and hardness of A357 aluminum alloy fabricated by selective laser melting

Effect of Selective Laser Melting Process Parameters on the Quality of Al Alloy Parts: Powder Characterization, Density, Surface Roughness, and Dimensional Accuracy

Analyzing the effects of powder and post-processing on porosity and properties of electron beam melted Ti-6Al-4V

Correlation between surface texture and internal defects in laser powder-bed fusion additive manufacturing

Effects of scanning parameters on material deposition during Electron Beam Selective Melting of Ti-6Al-4V powder

Effect of post-processing on microstructure and mechanical properties of Alloy 718 fabricated using powder bed fusion additive manufacturing processes

Influence of AlSi10Mg Particles Microstructure on Heat Conduction During Additive Manufacturing

The Effect of Energy Density on Microstructural, Mechanical, and Corrosion Characteristics of Ti-6Al-4V Alloy Fabricated via Selective Laser Melting and Electron Beam Melting Techniques

Effect of Powder Spreading Parameters on Laser Absorption Behavior and Processability of High‐Strength Aluminum Alloy Fabricated by Laser Powder Bed Fusion

Pore Formation Driven by Particle Impact in Laser Powder-Blown Directed Energy Deposition.

Influence of powder characteristics on microstructure and mechanical properties of Inconel 718 superalloy manufactured by direct energy deposition