Abstract:A 2000 W high power laser powder bed fusion technique (HP-LPBF) was used to fabricate 18Ni300 maraging steel in this study. The densification feature, microstructure and mechanical properties of the as-fabricated specimens were studied, as well as the influence of solution-aging heat treatment on the microstructure and mechanical properties. The results show that dense samples (relative density >99.5%) can be obtained when the laser energy density (E-v) is higher than 80 J/mm(3). A large quantity of columnar prior-austenite grains (PAGs) are observed within the as-fabricated samples, and a typical dendritic microstructure is shown inside the PAGs. Some ordered Ni(Al, Fe) intermetallics precipitates with diameters of 3-5 nm have formed as the result of the intrinsic heat treatment effect. With the increase of E-v, the average width of the PAGs and the average dendrite arm spacing are increased. The sample fabricated with the E-v of 111 J/mm(3) (short for HP-AF) has the best trade-off between build rate and mechanical properties among the as-fabricated samples. The build rate of the HP-AF sample is up to 18 mm(3)/s, which is about 3 times higher than that of the previous studies based on low power laser powder bed fusion. The yield strength (YS) (983 +/- 10 MPa), ultimate tensile strength (UTS) (1100 +/- 11 MPa) and elongation (El) (9.8 +/- 0.7%) of the HP-AF sample are comparable to those of the wrought 18Ni300. After solution-aging treatment, the austenite fraction increases from 4.4% (HP-AF) to 5.3%, whilst the Ti/Al rich nano precipitates with size 30-45 nm can be observed in the matrix. After solution-aging treatment, the YS and UTS of the sample (short for HP-ST + AT) are dramatically increased to 1945 +/- 12 MPa and 1865 +/- 8 MPa, though the elongation is decreased to 5.4 +/- 0.5%. The mechanical property of the HP-ST + AT samples is comparable to that of the wrought-aged 18Ni300. The high strength of the HP-ST + AT 18Ni300 sample is mainly attributed to precipitation strengthening as well as dislocation strengthening, followed by grain boundary strengthening.

Effect of Powder Formulation and Energy Density on the Nitrogen Content, Microstructure, and Mechanical Properties of SLMed High-Nitrogen Steel

Effect of beam energy density characteristics on microstructure and mechanical properties of Nickel-based alloys manufactured by laser directed energy deposition

Nitriding Behaviour and Microstructure of High-Nitrogen Stainless Steel during Selective Laser Melting

Effects of the process parameters on the formability and properties of Ni54(at.%) Ti alloys prepared by laser powder bed fusion

Effect of Aluminium Content and Processing Parameters on the Microstructure and Mechanical Properties of Laser Powder-Bed Fused Magnesium-Aluminium (0, 3, 6, 9wt%) Powder Mixture

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Effect of process parameters on microstructure and mechanical properties of a nickel-aluminum-bronze alloy fabricated by laser powder bed fusion

Effect of Laser Energy Density on the Microstructure, Mechanical Properties, and Deformation of Inconel 718 Samples Fabricated by Selective Laser Melting

Effects of process parameters on the microstructure and mechanical properties of 24CrNiMo steel fabricated by selective laser melting

Microstructures and mechanical properties of powder-filled laser welding joints composed of high-nitrogen steel

Effect of Laser Energy Density on the Microstructure and Microhardness of Inconel 718 Alloy Fabricated by Selective Laser Melting

Influence of energy density on the microstructure and property regulation of additive manufactured pure nickel

Influence of Energy Density on the Microstructure and Mechanical Properties of GH5188 Superalloy Formed by Laser Melting Deposition

Microstructure and Mechanical Properties of Selective Laser Melting of Hydrogen Embrittlement Resistance Stainless Steel HR-2

Effects of Oxygen Content on Microstructure and Mechanical Properties of 18ni300 Maraging Steel Manufactured by Laser Directed Energy Deposition

Effect of Volume Energy Density on Selective Laser Melting Niti Shape Memory Alloys: Microstructural Evolution, Mechanical and Functional Properties

Investigation on the Attainment of High-Density 316L Stainless Steel with Selective Laser Sintering

Austenitic Stainless Steel Powders with Increased Nitrogen Content for Laser Additive Manufacturing

Research status on the effect of energy density on the forming microstructure and properties of nickel-based superalloys for laser additive manufacturing

High Power Laser Powder Bed Fusion of 18ni300 Maraging Steel Processing Optimization, Microstructure and Mechanical Properties

Effect of a constant laser energy density on the evolution of microstructure and mechanical properties of NiTi shape memory alloy fabricated by laser powder bed fusion