High Power Laser Powder Bed Fusion of 18ni300 Maraging Steel Processing Optimization, Microstructure and Mechanical Properties

Gao Huang,Kaiwen Wei,Jinfeng Deng,Xiaoyan Zeng

DOI: https://doi.org/10.1016/j.msea.2022.143983

IF: 6.044

2022-01-01

Materials Science and Engineering A

Abstract:A 2000 W high power laser powder bed fusion technique (HP-LPBF) was used to fabricate 18Ni300 maraging steel in this study. The densification feature, microstructure and mechanical properties of the as-fabricated specimens were studied, as well as the influence of solution-aging heat treatment on the microstructure and mechanical properties. The results show that dense samples (relative density >99.5%) can be obtained when the laser energy density (E-v) is higher than 80 J/mm(3). A large quantity of columnar prior-austenite grains (PAGs) are observed within the as-fabricated samples, and a typical dendritic microstructure is shown inside the PAGs. Some ordered Ni(Al, Fe) intermetallics precipitates with diameters of 3-5 nm have formed as the result of the intrinsic heat treatment effect. With the increase of E-v, the average width of the PAGs and the average dendrite arm spacing are increased. The sample fabricated with the E-v of 111 J/mm(3) (short for HP-AF) has the best trade-off between build rate and mechanical properties among the as-fabricated samples. The build rate of the HP-AF sample is up to 18 mm(3)/s, which is about 3 times higher than that of the previous studies based on low power laser powder bed fusion. The yield strength (YS) (983 +/- 10 MPa), ultimate tensile strength (UTS) (1100 +/- 11 MPa) and elongation (El) (9.8 +/- 0.7%) of the HP-AF sample are comparable to those of the wrought 18Ni300. After solution-aging treatment, the austenite fraction increases from 4.4% (HP-AF) to 5.3%, whilst the Ti/Al rich nano precipitates with size 30-45 nm can be observed in the matrix. After solution-aging treatment, the YS and UTS of the sample (short for HP-ST + AT) are dramatically increased to 1945 +/- 12 MPa and 1865 +/- 8 MPa, though the elongation is decreased to 5.4 +/- 0.5%. The mechanical property of the HP-ST + AT samples is comparable to that of the wrought-aged 18Ni300. The high strength of the HP-ST + AT 18Ni300 sample is mainly attributed to precipitation strengthening as well as dislocation strengthening, followed by grain boundary strengthening.