Abstract:Powder metallurgy (PM) α + β Ti-4Al-4Mo-4Sn-0.5Si alloys were fabricated through thermomechanical powder consolidation of TiH 2 -based powder compacts with two different processing routes: one involving blending the elemental powders (BE route) and the other involving mechanical milling a blend of elemental powders (MM route). With the MM + annealing + solution and aging (STA) route, a hierarchical microstructure consisting of necklace-like micron-scaled grain boundary α (α GB ) segments and isolated submicron-scaled primary α (α p ) rods dispersed in a β transformed structure (β t ) matrix containing a high number density of nano-scaled secondary α (α s ) laths was produced in the alloy. The alloy with the hierarchical microstructure achieved an excellent combination of a very high yield strength of 1339 MPa,an ultimate tensile strength of 1467 MPa and an excellent ductility of 10.4%. The increased strength was mainly due to the high fraction of β t matrix in which the fine-dispersed α s precipitates with different orientations efficiently blocked the dislocation motion during deformation. The excellent ductility achieved despite of the high flow stress can be attributed to the elimination of strain concentration in the α GB segments which prevented their cracking prior to the material reaching the necking point during plastic deformation. This was in contrast with the typical α/β t lamellar microstructure of the same alloy composition obtained with the BE + same heat treatment route where strain concentration in the α GB plates occurred due to the direct slip transmission from α colonies to adjacent parent α GB grains during plastic deformation, thus resulting in intergranular premature cracking. TEM observation demonstrated that the strain gradient from the α/β t interfaces to the domain interiors of both α GB segments and α p rods activated a high density of geometrically necessary dislocations near the interfaces, and caused an obvious synergistic strengthening effect which also contributed to the slow drop of strain hardening rate and thus was beneficial to improving the ductility.

Micro-nano Secondary Phase Greatly Increases the Plasticity of Titanium-Zirconium-molybdenum Alloy

Achieving Enhanced Tensile Strength-Ductility Synergy Through Phase Modulation in Additively Manufactured Titanium Alloys

ZrTiO4 secondary phase effects on ductility and toughness of molybdenum alloys

Microstructure Regulation and Strength-Elongation Synergy of the Near Alpha TZAM Alloy Via Thermomechanical Processing

Secondary phases effects on microstructure and mechanical properties of lanthanum-doped titanium‐zirconium‐molybdenum alloy

The formation mechanism of micro-nano secondary phase in solid-liquid doped TZM alloy

Enhanced Mechanical Properties of Ti-5Al-5Mo-5V-3Cr-1Zr by Bimodal Lamellar Precipitate Microstructures Via Two-Step Aging

Influence of Multiphase Microstructure on the Strength and Ductility of Nb-Zr-Ti-V Refractory High Entropy Alloys

Hierarchical microstructure and strain partition of a PM α + β titanium alloy with an ultrahigh strength-ductility synergy

Achieving super-high strength and acceptable plasticity for a near β-type Ti-4.5Mo-5.1Al-1.8Zr-1.1Sn-2.5Cr-2.9Zn alloy through manipulating hierarchical microstructure

Making Titanium Alloys Ultrahigh Strength and Toughness Synergy Through Deformation Kinks-Mediated Hierarchical Α-Precipitation

Achieving Synergy Between Strength and Ductility in Metastable Β-Titanium Alloy Through a Novel Multi-Morphological Microstructure

Ultrahigh strength and large plasticity of nanostructured Ti62Nb12.2Fe13.6Co6.4Al5.8 alloy obtained by selectively controlled micrometer-sized phases

Effect of secondary phases on the strength and elongation of a novel Mo-TiC-ZrC-C alloy

Evaluation of tensile property and strengthening mechanism of Zirconia reinforced molybdenum alloy

Breaking the high-temperature strength-ductility trade-off in TiAl alloys through microstructural optimization

Tuning the Morphology of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy: from Brittle to Ductile Fracture

Evading the strength-ductility trade-off at room temperature and achieving ultrahigh plasticity at 800°C in a TiAl alloy

Achieving synergy enhancement of strength and ductility in Ti-6Al-2Sn-4Zr-2Mo-0.1Si alloy by fabricating a new multiscale microstructure

Design and microstructure-mechanical properties of a novel metastable β titanium alloy with excellent strength-plasticity matching

Examination of Novel Titanium-639 Alloy as a Means of Balancing Strength and Ductility through Molybdenum Addition Rather than Prolonged Aging Heat Treatment