Examination of Novel Titanium-639 Alloy as a Means of Balancing Strength and Ductility through Molybdenum Addition Rather than Prolonged Aging Heat Treatment

Shiraz Mujahid,Alireza Fadavi Boostani,YubRaj Paudel,Andrew Oppedal,Bhasker Paliwal,Hongjoo Rhee,Haitham El Kadiri
DOI: https://doi.org/10.3390/met14070828
IF: 2.695
2024-07-19
Metals
Abstract:Manufacturing titanium alloys with simultaneous enhancement in strength and ductility has motivated extensive research into various strategies for regulating the arrangement and texture of α and β phases. The present study explores a novel α + β titanium alloy, TIMETAL 639 (Ti-639), produced by replacing a portion of vanadium in Ti-64 with molybdenum. The low diffusivity and β-stabilizing effects of molybdenum help retain bimodal characteristics within solution heat-treated Ti-639 microstructures. EBSD and TEM were used to examine β-phase evolution after thermal processing and recrystallization of new globular α grains within pre-existing colonies in a depleted bimodal microstructure. These depleted bimodal colonies in solution heat-treated Ti-639 also led to lower misorientation spreads and dislocation densities within neighboring primary α grains. Quasi-static compression along the plate normal direction demonstrated the ability of the depleted bimodal microstructure to simultaneously enhance strength and ductility in Ti-639 (~90 MPa stronger, ~6% higher failure strain) versus identically processed Ti-64. Only one solution heat-treatment step (1 h at 900 °C) is needed to achieve these properties in Ti-639, whereas comparable properties in Ti-64 required prolonged aging heat treatment (24 h at 600 °C) after the same solution heat-treatment step, making Ti-639 a viable α + β alloy candidate.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?