High-Temperature Atomic Layer Deposition of Rutile TiO 2 Films on RuO 2 Substrates: Interfacial Reactions and Dielectric Performance

Jihoon Jeon,Taikyu Kim,Myoungsu Jang,Hong Keun Chung,Sung-Chul Kim,Sung Ok Won,Yongjoo Park,Byung Joon Choi,Yoon Jang Chung,Seong Keun Kim

DOI: https://doi.org/10.1021/acs.chemmater.3c03324

IF: 10.508

2024-03-28

Chemistry of Materials

Abstract:Capacitor structures utilized in modern dynamic random access memory (DRAM) cells require the conformal growth of high-k films on electrode materials. In this context, the atomic layer deposition (ALD) of rutile-phase TiO2 on nearly lattice-matched substrates such as RuO2 has been extensively explored. It is typically desired to grow such insulating films at high temperatures to ensure low defect concentrations and high crystallinity. However, with increasing growth temperature, it is also crucial to consider the aggravated effect of interface reactions that could potentially hinder final device performance. Here, we report the high-temperature ALD growth of TiO2 on RuO2 substrates using the heteroleptic precursor trimethoxy­(pentamethylcyclopentadienyl)­titanium ((CpMe5)­Ti­(OMe)3) and O3. High-quality, rutile-phase TiO2 films with large dielectric constants of ∼100 could be grown at temperatures exceeding 300 °C. When the growth temperature reaches 330 °C, we find that an anomalous RuO2 reduction reaction occurs due to interactions between the substrate and Ti precursor. The reduced Ru is transformed into volatile RuO4 during the subsequent O3 injection steps, resulting in partial etching of the substrate. Simple RuO2/TiO2/RuO2 capacitor devices fabricated from optimized films demonstrate excellent dielectric performance with an equivalent oxide thickness (EOT) of 0.5 nm at leakage current densities of less than 10–7 A/cm2. A further reduction of EOT to 0.4 nm could be achieved by implementing a single cycle of Al doping to the TiO2 films, surpassing the benchmark values proposed for next-generation DRAM capacitors by a safe margin. Our findings clearly showcase the benefits of high-temperature ALD in the semiconductor technology, as well as providing guidelines for the interpretation of the convoluted interface reactions tied to its implementation.

materials science, multidisciplinary,chemistry, physical