Abstract:With the development of product miniaturization in aerospace and other fields, nickel-based superalloy thin sheets with excellent comprehensive properties have become crucial materials for micro-components in these fields. Due to the complexity of the initial microstructure and strengthening mechanism, there is a lack of in-depth research on the mesoscale formability of nickel-based superalloys under the coupled effects of multiple factors such as feature size (i.e., the ratio of specimen thickness to grain size, t / d ), particle size and volume content of the precipitated phase. In this paper, a test platform was constructed for the application of high-precision strain measurements to the analysis of the mesoscale forming limit, and the mechanisms for the influences of feature size and precipitation on the mesoscale forming limit of a nickel-based superalloy were studied. The results showed that feature size influenced the forming limit of the nickel-based superalloy thin sheet at the mesoscopic scale, and the formability decreased with decreasing t / d and increasing γ′′/γ′ particle size and volume content. Based on surface layer theory and ductile fracture theory, the influences of t / d and γ′′/γ′ phases on the forming limit of nickel-based superalloy thin sheets at the mesoscopic scale were revealed. The coupled effects of surface roughening caused by free surface grains and hindered dislocation movement induced by precipitated phases resulted in strain localization and reduced the forming properties of nickel-based superalloy thin sheets at the mesoscopic scale.

Size-dependent Microstructure Evolution and Formation Mechanisms During the Gas Atomization Process of FGH4113A Ni-based Superalloy Powder

Nucleation on Thermal History and Microstructural Evolution of Atomized Ti-48Al Nano and Micro-Powders

Particle Size Dependence of the Microsegregation and Microstructure in the Atomized Ni-based Superalloy Powders: Theoretical and Experimental Study

Microstructural Feature and Evolution of Rapidly Solidified Ni 3 Al-Based Superalloys

Effects of composition and particle size on the surface state and degassing behavior of nickel-based superalloy powders

Dendrite evolution and quantitative characterization of γ′ precipitates in a powder metallurgy Ni-based superalloy by different cooling rates

Study on Powder Characteristics and Effect Factors of Droplets Size During Electrode Induction Melting Gas Atomization

Probing the formation mechanism of hierarchical microstructures in experimental Ni-based superalloys

Unraveling the Formation Mechanism of Abnormally Large Grains in an Advanced Polycrystalline Nickel Base Superalloy

Microstructural Evolution of Al–Ni–Y Powders with Different Sizes

Microstructural Evolution with a Wide Range of Solidification Cooling Rates in a Ni-Based Superalloy

Microstructure, Segregation and Precipitate Evolution in Directionally Solidified GH4742 Superalloy

Characterization of the Microstructure Evolution and Microsegregation in A Ni-Based Superalloy under Super-High Thermal Gradient Directional Solidification

Morphology Evolution of Γ′ Precipitates in a Powder Metallurgy Ni-base Superalloy

Microstructure characteristics of superalloy powders during rapid solidification prepared by argon atomisation

Solidification microstructure of FGH96 superalloy powder prepared by argon gas atomization

Microstructure Optimization for Higher Strength of a New Fe–Ni-based Superalloy

The Influence of Cooling Rate on the Microstructure and Phase Fraction of Gas Atomized NiAl3 Alloy Powders During Rapid Solidification

The Effect of the Nucleation Ability on Solidified Microstructures of Gas-Atomized Fe–6.5 Wt.%si Alloy Powder

Solidification Microstructure of Directionally Solidified Superalloy under High Temperature Gradient

Size effect on the forming limit of a nickel-based superalloy thin sheet at the mesoscopic scale