Effect of humid atmosphere on the microstructure and mechanical properties of a PM Ni-based superalloy: From powders to bulk alloys
Qiang Zhang,Liang Zheng,Hua Yuan,Zhou Li,Guoqing Zhang,Jianxin Xie
DOI: https://doi.org/10.1016/j.matchar.2023.113019
IF: 4.537
2023-05-23
Materials Characterization
Abstract:Understanding the effects of powder storage condition is helpful to improve the mechanical properties of powder metallurgy (PM) and additive manufacturing (AM) superalloys. In this work, nickel-based FGH96 superalloy powders were stored under ambient air (relatively dry) and humid (25 °C/95%RH and 90 °C/95%RH) atmospheres and then consolidated by hot isostatic pressing (HIP). The powders and corresponding bulk alloys were characterized by XPS, OM, FESEM, EPMA, EBSD, and TEM. The results indicate that the humid atmosphere mainly affects the gas content, chemical state, and oxide/hydroxide layer thickness of powders, leading to highest values of oxygen content (~450 ppm), hydrogen content (~25 ppm), and NiO/Ni(OH) 2 thickness (~13.9 nm) for 90 °C/95%RH powders, and further forms much severe prior particle boundaries (PPBs) defects in HIPed alloy. The detrimental PPBs are composed of large-sized γ', MC carbides-(Ti, Nb)C, Al 2 O 3 and ZrO 2 oxides. In comparison with ambient air powders compact, the strength of 90 °C/95%RH powders compact is unexpectedly increased, which is due to the internal grains pinned inside the original particle boundaries by higher severity degree of PPBs, and leads to the increase of grain boundary strength. Meanwhile, the ductility is significantly decreased, because the fracture mode transited from ductile transgranular fracture to brittle inter-particle debonding. The study reveals the relationship between humid atmosphere and properties of both powders and bulk alloys, and intends to obtain good combination of strength and ductility for PM Ni-based superalloys.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing