Abstract:Cryogenic rolling experiments have been conducted on the AZ31 magnesium (Mg) alloy sheet with bimodal non-basal texture, which is fabricated via the newly developed equal channel angular rolling and continuous bending process with subsequent annealing (ECAR-CB-A) process. Results demonstrate that this sheet shows no edge cracks until the accumulated thickness reduction reaches about 18.5%, which is about 105.6% larger than that of the sheet with traditional basal texture. Characterization experiments including optical microstructure (OM), X-ray diffractometer (XRD), and electron backscatter diffraction (EBSD) measurements are then performed to explore the microstructure characteristics, texture evolution and deformation mechanisms during cryogenic rolling. Experimental observations confirm the occurrence of abundant {10–12} extension twins (ETs), twin-twin interactions among {10–12} ET variants and {10–12}-{10–12} double twins (DTs). The twinning behaviors as for {10–12} ETs are responsible for the concentration of c-axes of grains towards normal direction (ND) and the formation of transverse direction (TD)-component texture at the beginning of cryogenic rolling. The twinning behaviors with respect to {10–12}-{10–12} DTs are responsible for the disappearance of TD-component texture at the later stage of cryogenic rolling. The involved deformation mechanisms can be summarized as follows: Firstly {10–12} ETs dominate the plastic deformation. Subsequently, dislocation slip, especially basal slip, starts to sustain more plastic strain, while {10–12} ETs occur more frequently and enlarge continuously, resulting in the formation of twin-twin interaction among {10–12} ET variants. With the increasing rolling passes, {10–12}-{10–12} DTs incorporate in the plastic deformation and dislocation slip serves as the major one to sustain plastic strain. The activities of basal slip, {10–12} ETs and {10–12}-{10–12} DTs benefit in accommodating the plastic strain in sheet thickness, which contributes to the improved rolling formability in AZ31 Mg alloy sheet with bimodal non-basal texture during cryogenic rolling.

Twinning-mediated Texture Weakening in a Basal-Textured Mg-6Al-1Zn (mass%) Alloy Sheet by a Novel Cold-Sample Rolling Method

Unexpectedly Formed Strong Basal Texture in a Rolled Mg-Zn-Ca-Mn Alloy Sheet

Texture weakening and ductility improvement of Mg-1.1Mn-0.5Al alloy via medium temperature-high reduction rolling: twinning variants selection and dynamic recrystallization mechanism

Twinning-Assisted Static Recrystallization and Texture Evolution in A Mg-Gd-Y-Zr Alloy

Formation of Unusual Rolling Texture in a Mg-Al-Mn Alloy Sheet by Large-Strain Hot-Rolling

Tailoring the Texture and Mechanical Properties of Textured-AZ31 Mg Alloy Sheets by Twinning and Recrystallization

Twinning, Grain Orientation, and Texture Variations in Mg Alloy Processed by Pre-Rolling

Influence of Bimodal Non-Basal Texture on Microstructure Characteristics, Texture Evolution and Deformation Mechanisms of AZ31 Magnesium Alloy Sheet Rolled at Liquid-Nitrogen Temperature

Effect of Al addition and rolling reduction on microstructure and texture evolution of Mg–3Sn alloy during high-speed rolling

Origin of Extension Twinning-Mediated Static Recrystallization and Unique Parallel Alignment of (0001) Poles to Transverse Direction in Mg-3Al-0.4Mn (mass%) Alloy Sheet

Twinning Behavior of a Strongly Basal Textured AZ31 Mg Alloy During Warm Rolling

Understanding the mechanisms of texture evolution in an Mg-2Zn-1Ca alloy during cold rolling and annealing

Texture Optimization on Mg Sheets by Preparing Soft Orientations of Extension Twinning for Rolling

Insights into the evolution of texture and mechanical properties during warm rolling and annealing of Mg–2Zn-0.5Ca alloy

Achieving a Weak Basal Texture in a Mg–6Al–3Sn Alloy by Wave-Shaped Die Rolling

Activation of {1 01¯2} Twinning and Slip in High Ductile Mg–2.0Zn–0.8Gd Rolled Sheet with Non-Basal Texture During Tensile Deformation at Room Temperature

Twinning and Mechanical Behavior of an Extruded Mg–6Al–3Sn Alloy with a Dual Basal Texture

Unusual Twin Induced Recrystallization and Corresponding Texture Optimization in a Cold Rolled Mg-Gd-Zr Alloy During Annealing

Multiple-twinning induced recrystallization and texture optimization in a differential-temperature-rolled AZ31B magnesium alloy with excellent ductility

Texture Evolution During Cold Rolling of Dilute Mg Alloys

Twinning character and texture origination in the randomly-oriented AZ31B magnesium alloy during cold-rolling