Abstract:The influence of Mo (10‐40at.%) additions to Cr‐8at.%Si was systematically studied by producing arc melted alloys and analyzing the as‐cast and annealed microstructures as well as the oxidation resistances. The majority of the alloys contained a solid solution A2 matrix with the intermetallic A15 = (Cr,Mo)3Si phase. The oxidation resistance was tested by thermogravimetric analysis (TGA) at 1200 °C in air for 50 and 100 h. Samples were characterized by XRD, SEM and EPMA (WDS). The studied Cr‐xMo‐8Si alloy series showed a beneficial effect of Mo on the corrosion behavior of the annealed arc melted alloys exposed at 1200 °C in air. An increased amount of A15 led to the formation of a continuous SiO2 scale beneath the Cr2O3 layer during high temperature exposure. The internal SiO2 layer inhibited further internal oxidation of the A15 phase. Prior annealing also influenced the oxidation behavior of the alloys. Higher annealing temperatures, resulted in an overall reduced fraction of the A15 phase, as well as coarsening, but also showed a more uniform size and distribution of the precipitates, which seems to benefit the formation of a protective duplex oxide scale. Cr‐25Mo‐8at.%Si annealed at 1350 °C for 100 h, showed the most promising oxidation behavior after exposure in air at 1200 °C for 100 h. For all of the investigated Mo contents, no nitridation was observed when compared to the Cr‐8Si reference composition. The oxide scale adhesion also was improved. For Mo >25 at.% no spallation was observed. Evaluation of the TGA data showed it follows the paralinear law, with both the growth rate, kp, and volatilization rate, kv, of Cr2O3 being reduced by adding 10‐25 at.% Mo. A binary Cr/Mo‐Si phase diagram was generated for the studied alloy series in order to determine accurate annealing conditions and estimate the stability range of the metastable σ phase. This article is protected by copyright. All rights reserved.

High-temperature Oxidation Behaviour of SPS-prepared Mo and Mo–5Ta Alloys

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

Effect of Ti and Ta content on the oxidation resistance of Co-Ni-based superalloys

High-temperature steam oxidation behavior of an FeCrAl alloy with controlled addition of Mo

The oxidation mechanism of nanostructured Y-Zr-O complex oxide dispersion-strengthened Mo alloys

Microstructure Evolution and Oxidation Mechanism of Ta5 Titanium Alloy During High-Temperature Heat Treatment

Oxidation behavior of multi-component Ta–W–Al–Ti alloy at 1173 K

Microstructure refinement and oxidation behavior improvement in Mo modified TiAl4822 alloy prepared by vacuum sintering

Insight into the Ta alloying effects on the oxidation behavior and mechanism of cast TiAl alloy

High-Temperature Oxidation of NbTi-Bearing Refractory Medium- and High-Entropy Alloys

Preparation and enhanced oxidation behavior of microalloyed Mo5SiB2 alloy at 1300 °C

Effect of microalloying with silicon on high temperature oxidation resistance of novel refractory high-entropy alloy Ta-Mo-Cr-Ti-Al

Influence of TiC contents on the microstructure, mechanical properties, and oxidation behavior of Mo–10Si–8B alloys

Oxidation behavior of Ti-Nb-Mo-Al-Six refractory high entropy alloy at 1000°C

Effects of Ta Addition on the Microstructure, Compression Properties and Oxidation Resistance of NiAl-Cr(Mo) Alloy

High-Temperature Oxidation Behavior of Refractory High-Entropy Alloys: Effect of Alloy Composition

Oxidation Protection of High-Temperature Coatings on the Surface of Mo-Based Alloys—A Review

Oxidation Behavior of (Mo,Hf)Si2-Al2O3 Coating on Mo-Based Alloy at Elevated Temperature

THE INFLUENCE OF Mo‐CONTENT AND ANNEALING ON THE OXIDATION BEHAVIOUR OF ARC‐MELTED Cr‐xMo‐8Si ALLOYS

High Temperature Oxidation Behavior of Directionally Solidified Fe(Al,Ta)/Fe2Ta(Al) Eutectic Composite