Abstract:High-performance engineering alloys, such as 7000 series aluminum alloys, suffer poor printability in laser powder bed fusion (LPBF) additive manufacturing. An enormous challenge lies in the suppression of solidification cracks caused by solidification shrinkage and thermal stresses. Porosity formation, as one of the main concerns for LPBF application, should also be avoided at the same time. In this study, aluminum alloy (AA) 7075 with and without Zr modification was additively manufactured by LPBF. Processing parameters of laser power and scanning speed, resulting in various volumetric energy density (VED), were experimentally determined to produce crack-free components with tailored microstructure. Optical microscopy was used to reveal how the crack density and porosity vary with VED. Scanning electron microscopy and transmission electron microscopy uncovered the detailed microstructure in the molten pool and the evolution of the elemental Zr addition. The results indicate that 1 w.t.% addition of elemental Zr in AA7075 led to lower crack density compared with 0.3 w.t.% addition. In 1 w.t.% Zr-modified AA7075, crack-free components were obtained under high VED. Fine equiaxed grains, instead of large columnar grains, were formed at the bottom of the molten pool boundary due to the existence of Al3Zr compound, which favored the nucleation of aluminum grains and elimination of cracks. The phenomenon of silicon segregation near cracks remained in Zr modified alloys, although its effects on cracking were suppressed. Spherical pores in the Zr-modified AA7075 increased due to the deterioration of fluidity by unmelted particles, which distracted the Marangoni flow as well. Sufficient laser energy input can increase the viscosity and ease the pores escaping. By optimizing parameters, crack-free AA7075 parts with low porosity can be manufactured through LPBF with Zr addition.

Role of Er on the Densification, Microstructure and Mechanical Properties of 7075 Aluminium Alloys Manufactured by Laser Powder Bed Fusion

Influence of erbium addition on the defects of selective laser-melted 7075 aluminium alloy

Effect of Er Addition on the Microstructure, Mechanical Properties and Corrosion Behaviour of Al-Zn-Mg-Cu Alloy Manufactured by Laser Powder Bed Fusion

Processing and characterization of crack-free 7075 aluminum alloys with elemental Zr modification by laser powder bed fusion

Microstructure and mechanical properties of Al-Mg-Mn-Er-Zr alloys fabricated by laser powder bed fusion

Effect of Er and Zr additions and aging treatment on grain refinement of aluminum alloy fabricated by laser powder bed fusion

Microstructure, mechanical properties, and crack formation of aluminum alloy 6063 produced via laser powder bed fusion

A Novel Al-Zn-Mg-Cu-Si-Zr-Er Alloy Fabricated by Laser Powder Bed Fusion

Microstructure, mechanical properties and fatigue crack growth behavior of an Al-Zn-Mg-Cu-Si-Zr-Er alloy fabricated by laser powder bed fusion

Effect of Aluminium Content and Processing Parameters on the Microstructure and Mechanical Properties of Laser Powder-Bed Fused Magnesium-Aluminium (0, 3, 6, 9wt%) Powder Mixture

Facile and cost-effective approach to additively manufacture crack-free 7075 aluminum alloy by laser powder bed fusion

Microstructure characterization and mechanical properties of crack-free Al-Cu-Mg-Y alloy fabricated by laser powder bed fusion

Effect of Powder Spreading Parameters on Laser Absorption Behavior and Processability of High‐Strength Aluminum Alloy Fabricated by Laser Powder Bed Fusion

Laser powder bed fusion of an Al-Cr-Fe-Ni high-entropy alloy produced by blending of prealloyed and elemental powder: process parameters, microstructures and mechanical properties

Laser powder bed fusion of nano-titania modified 2219 aluminium alloy with superior mechanical properties at both room and elevated temperatures: The significant impact of solute

Effect of post-heat treatment on the microstructure, mechanical, and corrosion properties of laser powder bed fused Al–Zn–Mg–Cu–Si–Zr–Er alloys

Effect of laser power on the microstructure and mechanical properties of laser-assisted cold sprayed 7075 aluminum alloy deposits

Fabrication of crack-free aluminum alloy 6061 parts using laser foil printing process

Laser powder bed fusion of crack-free TiN/Al7075 composites with enhanced mechanical properties

Enhanced Strength–Corrosion Synergy of 6061Al Casting Alloy Through Erbium Addition

Tailored porosity in additive manufacturing of 7075 aluminum alloy for crack suppression and high strength