Abstract:The effects of rare earth erbium (Er) micro-additions on the microstructures and mechanical properties of 2024 aluminum alloy were investigated. The microstructures and fracture surfaces of specimens prepared via high-energy ball milling, cold isostatic pressing and microwave sintering were carried out by optical microscopy (OM) and scanning electron microscopy (SEM). Under the conditions of sintering heating rate of 20 min/°C and soaking time of 30 min at 490 °C, it was found that with the increase in Er addition, the grain size first decreased then increased, and it reached a minimum size of about 5 μm when the Er content was 0.6%, showing that the grains were refined. At the same time, the compactness and microhardness reached maximum levels, which were 97.6% and 94.5 HV, respectively. Moreover, the tensile strength and elongation reached the peak at 160.5 MPa and 4.4%, respectively. The dynamic mechanical response of Er/2024Al alloy with different Er content was studied through a split Hopkinson pressure bar (SHPB) at strain rates of 600 s−1 and 800 s−1, respectively. Both at the strain rates of 600 s−1 and 800 s−1, the dynamic yield stress of the specimens increased gradually with an increase in Er content. For the 0.6 wt.% Er specimen, the dynamic yield stress reached 371.3 MPa at a strain rate of 800 s−1, which was 28.2% higher than that at a strain rate of 600 s−1. When the strain rate is 800 s−1, the deformation degree of the 0.6 wt.%Er specimen is 55.3%, which is 14.7% higher than for the Er-free one, and there are adiabatic shear bands formed in the 0.6 wt.%Er specimen. Through a fracture analysis of the samples, a certain number of dimples appeared in the fracture of an impact specimen, indicating that the addition of Er improved the toughness of the material. This research can provide a reference for the development and application of high-performance aluminum alloy in automotive structural materials.

Influence of erbium addition on the defects of selective laser-melted 7075 aluminium alloy

Processing and characterization of crack-free 7075 aluminum alloys with elemental Zr modification by laser powder bed fusion

Effect of Erbium Micro-Additions on Microstructures and Properties of 2024 Aluminum Alloy Prepared by Microwave Sintering

Study on the laser selective melting and forming process and organizational properties of a TiSi 2 -modified 7075 aluminum alloy

Si-Assisted Solidification Path and Microstructure Control of 7075 Aluminum Alloy with Improved Mechanical Properties by Selective Laser Melting

Effect of aging treatment on phase evolution and mechanical properties of selective laser melted Al-Mg-Er-Zr alloy

Microstructure and Mechanical Properties of an Er-Modified Al–Mg–Mn–Sc–Zr Alloy Processed by Selective Laser Melting

Effect of Er and Zr addition on laser weldability of AlSi10Mg alloys fabricated by selective laser melting

Enhanced Strength–Corrosion Synergy of 6061Al Casting Alloy Through Erbium Addition

Microstructure and mechanical properties of Al-Mg-Mn-Er-Zr alloys fabricated by laser powder bed fusion

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

A novel strategy to additively manufacture 7075 aluminium alloy with selective laser melting

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Effects of rare earth Er additions on microstructure development and mechanical properties of die-cast ADC12 aluminum alloy

Effect of Er and Zr additions and aging treatment on grain refinement of aluminum alloy fabricated by laser powder bed fusion

Densification, Microstructure and Anisotropic Corrosion Behavior of Al-Mg-Mn-Sc-Er-Zr Alloy Processed by Selective Laser Melting

Improved strength and ductility on laser beam welded joints of 7085Al matrix nanocomposites by in-situ ZrB 2 nanoparticles and Al 3 (Er, Zr) nanoprecipitates

Effect of Minor Er Additions on the Microstructures and Mechanical Properties of Cast Al-Cu-Mg-Ag Alloys

Selective laser melting of 7075 aluminum alloy inoculated by Al–Ti–B: Grain refinement and superior mechanical properties

Effect of Sm + Er and Heat Treatment on As-Cast Microstructure and Mechanical Properties of 7055 Aluminum Alloy

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting