Abstract:The study demonstrates that applying an electric current during solidification significantly refines the primary Si phase. Moreover, adding phosphorus enhances this effect, particularly at 10 ppm, which is below the critical threshold of 20 ppm. The combined approach leads to improved nucleation and dispersion of aluminum phosphide, optimizing the microstructure for enhanced alloy performance. The efficient processing of hypereutectic Al–Si alloys depends on controlling the microstructure of the primary Si phase during solidification. This study investigates the effects of electric current and phosphorus (P) addition on the refinement of primary Si, with the results confirming that applying electric current during solidification refines the primary Si phase; introducing P further enhances this refinement. Notably, when 10 ppm of P is added (below the identified critical amount of 20 ppm), an improved refinement effect is observed compared with the application of either electric current or P alone. Applying an electric current generates a circulating flow within the melt, resulting in an increased cooling rate, which leads to improved nucleation behavior for the primary Si phase. In addition, the circulating flow generated within the melt influences the dispersion of aluminum phosphide during nucleation. Adding P at concentrations above 40 ppm does not yield further benefits, suggesting a saturation point for its efficacy. This study demonstrates that the concurrent electric current application and minimal P addition can significantly enhance the refinement of primary Si phases, offering a potent approach for optimizing the microstructural properties of hypereutectic Al–Si alloys.

Refinement of Primary Si in Hypereutectic Al-Si Alloy by Serpentine Channel with Spoiler

Simultaneous Refinement of Primary Si and Modification of Eutectic Si in A390 Alloy Assisting by Sr-Modifier and Serpentine Pouring Channel Process

Study on the Effect of Pre-Refinement and Heat Treatment on the Microstructure and Properties of Hypoeutectic Al-Si-Mg Alloy

Influence of Rheo-Diecasting Processing Parameters on Microstructure and Mechanical Properties of Hypereutectic Al–30%Si Alloy

Refinement of Primary Si Phase in Hypereutectic Al–Si Alloy by Electrically Assisted Solidification with P Addition

Research Progress on Primary Phase Refinement in Hypereutectic Al-Si Alloys

Microstructure control and performance evolution of hypereutectic Al–20Mg2Si alloy by novel Al–Ca–Sb master alloy

Super-gravity field assisted homogeneous distribution of sub-micron eutectic Si in Al-Si alloy

Formation mechanism and conditions of fine primary silicon being uniformly distributed on single αAl matrix in Al-Si alloys

Enhancing Silicon Refinement in an Al-25Si Hypereutectic Alloy by High Cooling Rate and La–Ce–Y Modifiers

Preparation of semi-solid 6061 aluminum alloy slurry by serpentine channel pouring

Effects of Refinement and Modification on Melt Structure of Hypoeutectic Al-Si Alloy

Fabrication of hypereutectic Al Si alloy with improved mechanical and thermal properties by hot extrusion

Solidification microstructure manipulation mechanism of hypoeutectic and hypereutectic Al-Si alloys controlled by trace in-situ nano-Fe 2 B and nano-Fe 3 Si

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Achieving superior grain refinement efficiency for Al–Si casting alloys through a novel Al–La–B grain refiner

Microstructure Evolution of Primary Si Phase in Hypereutectic Al-20Si Alloys Prepared by Centrifugal Casting under an Electromagnetic Field

Synergistic Effect of Lanthanum and Melt Purification on the Microstructure of Hypereutectic Al–Si Alloy

Refinement of primary Si in Al–20%Si alloy by MRB through phosphorus additions

Microstructure and Thermal Conductivity of Hypereutectic Al-High Si Produced by Casting and Spray Deposition

Synergistic Effect of Strontium and Melt Quenching on the Solidification Microstructure of Hypereutectic Al-Si Alloys