Solidification microstructure manipulation mechanism of hypoeutectic and hypereutectic Al-Si alloys controlled by trace in-situ nano-Fe 2 B and nano-Fe 3 Si
Xiang-Yi Song,Ya-Jie Wang,Jing-Xin Zhang,Dong-Ao Du,Jin-Guo Xu,Fan Peng,Tao-Tao Li,Long-Jiang Zhang,Shi-Li Shu,Xin Li,Feng Qiu
DOI: https://doi.org/10.1016/j.jmrt.2022.10.142
IF: 6.267
2022-11-03
Journal of Materials Research and Technology
Abstract:In aluminum alloys, the most often utilized cast Al-Si alloy system, the microstructure often needs to be improved by modification and inoculation treatment. This study comprehensively examines the impact of nanocrystals produced by Fe-B-Si amorphous alloys on the solidification behavior and microstructure of hypoeutectic Al-Si 7 alloy and hypereutectic Al-Si 17 alloy. The nucleation temperature of α-Al is increased and the nucleation of α-Al is easier as well as crystallization platform becomes shorter. For primary Si, the nucleation temperature is decreased and the nucleation is inhibited. The eutectic transformation is promoted and the reaction time is shortened. For α-Al, in situ nano-Fe 2 B can act as its heterogeneous nucleation site and promote its nucleation. Meanwhile, the growth of α-Al dendrites is constrained by nearby grains and nanocrystals that do not participate in nucleation, therefore refining the dendrites. Furthermore, nano-Fe 2 B promotes the eutectic transformation and refines the eutectic microstructure. At the same time, the microstructure of the eutectic groups is refined and the distribution is more dispersed due to the confinement of finer adjacent grains and the hindrance of nanocrystals that do not participate in nucleation.
materials science, multidisciplinary,metallurgy & metallurgical engineering