Abstract:Numerous molecular dynamics (MD) simulations have been performed to investigate the effect of the nanopores on the martensitic transformation (MT) of pure iron (Fe) during the heating-cooling cycle. As per the simulation results, nanopores can obviously affect the difficulty on MT during the cooling process in two ways: On the one hand, the volume ratio of nanopores to simulation box model (R p/b ) can influence the distribution configuration of stacking fault (SF) to change the type of austenite microstructure during the heating process owing to the obstruction of the nanopores on the dislocation slip. The effect of nanopores is not obvious when R p/b is less than 2.22 %. The main type of austenitic changes from defect-free/simple-SF types to the intersecting-SF type and, finally, to the dislocation-cell type with an increase in R p/b from 2.22 % to 17.9 %. The dislocations in intersecting-SF type and dislocation-cell type austenitic microstructures can provide the nucleation site of MT, thus increasing the MT temperature. On the other hand, the high surface energy of the nanopores caused by the incomplete atomic lattice can provide the necessary energy for the nucleation of martensite, which then promotes the occurrence of MT during the cooling process. When the nanopores intersect with the dislocation wall in dislocation-cell type austenitic microstructure, martensite nucleates at the nanopores surface and then grows along the dislocation wall. In the previous investigation of selective laser melting martensitic steel, the nanopore in the microstructure was generally believed harmful to the mechanical property of specimen; however, in this study, it has been observed to promote the MT during solution-quenching heat treatment, which improves the mechanical property by improving the content of martensitic phase. This provides a new perspective in determining the significance of nanopores in microstructures.

Honeycomb Structure with Oxygen-Poor Pores at the Top of Magnetite Layer on a Martensitic Steel CLAM Exposed to Lead-Bismuth Eutectic at 500 ºc

Microstructure evolution of magnetite layer on CLAM steel exposed to lead-bismuth eutectic containing 10−6 wt% oxygen at 500 °C

Formation and dissolution of porous magnetite layer in contact with lead-bismuth eutectic: Locally equilibrium thermodynamic model

Insights into the Corrosion Mechanism of a 12cr F/M Steel in Oxygen-Saturated Liquid LBE

Microstructure Evolution and Yield Strength of CLAM Steel in Low Irradiation Condition

Growth of Inter-Metallic Compound Layers on CLAM Steel by HDA and Preparation of Permeation Barrier by Oxidation

Preliminary Experiments on the Corrosion of CLAM Steel in Flowing Eutectic LiPb

Structure of surface oxides on martensitic steel under simultaneous ion irradiation and molten LBE corrosion

Apparent Morphology and Structure of Martensite in Ultrahigh Carbon Steel

Mechanism analysis of grain refinement caused by deformation and the improvement of strength and ductility of CLAM steel

Honeycomb-like porous metallic glasses decorated by Cu nanoparticles formed by one-pot electrochemically galvanostatic etching

Early Corrosion Behavior of Low Carbon 9Cr-Ods Steel in High Temperature Oxygen-Saturated Lead-Bismuth Eutectic

The effect of nanopores on the mechanism of martensitic transformation in pure iron during the heating-cooling cycle: A molecular dynamics study

The Corrosion Behavior of Al/Al2O3 Composite Films with Ultra-Dense Structure Exposed to Lead-Bismuth Eutectic at 450 to 650 °C

Si Segregation and Relevant Effect on the Corrosion Propagation in F/M Steel Exposed to Liquid Lead-Bismuth Eutectic

Oxidation mechanism of refractory Molybdenum exposed to oxygen-saturated lead-bismuth eutectic at 600 °C

Preliminary Study Of Hda Coating On Clam Steel Followed By High Temperature Oxidation

Liquid metal embrittlement of 12Cr ferritic/martensitic steel thin-walled tubes exposed to liquid lead-bismuth eutectic

Microstructure of nano-structured ODS CLAM steel by mechanical alloying and hot isostatic pressing

Stabilities of the precipitates in CLAM steel during 30,000 h thermal aging

Liquid metal embrittlement susceptibility of an oxide-dispersion strengthened FeCrAl alloy in contact with liquid lead-bismuth eutectic at 350 °C