Abstract:This study aims to enhance the rheological behavior of SiC/Clay paste with the use of 3 types of polymers (CMC, PEG, and PVA) to obtain better printability through the Direct ink writing method pastes prepared by stirring polymer solutions with SiC/Clay powders. Rheometry and zeta potential tests are used to characterize pastes properties. 20 x 20 mm scaffolds were 3D printed then dried for 24h at room temperature and sintered at 1300°C for 1h to obtain the mullite phase in the final product. In this study, we investigated the impact of polyethylene glycol, sodium carboxymethyl cellulose, and polyvinyl alcohol on the rheological behavior, printability, and mechanical/physical properties of 3D‐printed scaffolds for high‐temperature applications using SiC/clay ceramic paste. Employing the Direct Ink Writing method, varying concentrations of each polymer (PEG: 2.5%–10% weight, CMC: .6%–1.8% weight, PVA: .25%–1% weight) were incorporated into the composition. The resulting SiC/clay paste, with adjusted additive content, was used to 3D‐print scaffold structures through Direct Ink Writing. Sintering of clay‐bonded SiC samples were carried out at 1300°C for 1 h in an ambient atmosphere. The research revealed that altering the additive amounts significantly influenced the rheological behavior, mechanical properties, and physical characteristics of the printed specimens. Notably, the ideal properties with additive concentrations (10% wt PEG, 1% wt PVA, and .6% CMC) were identified, providing the best outcomes in terms of printability and firing results. High density samples with 2.09, 1.93, and 1.79 g/cm3, high compression strength of 20.82, 14.5 and 12.53 MPa with 32.26%, 42.5%, and 52.63% open porosity for samples containing PVA, CMC, and PEG modifiers were obtained, respectively. Additionally, the study led to the development of a high solid loading printable paste with an 80% weight.

Rheological Behavior of Multi-Sized SiC Inks Containing Polyelectrolyte Complexes Specifically for Direct Ink Writing

Rheological Behavior of Al2O3 Suspensions Containing Polyelectrolyte Complexes for Direct Ink Writing

3D Printing of SiC Ceramic: Direct Ink Writing with a Solution of Preceramic Polymers

Mechanical and Dielectric Properties of Direct Ink Writing Si2N2O Composites

Phase Behavior of Polyelectrolyte Complexes and Rheological Behavior of Alumina suspensions for Direct Ink Writing

Optimization and Characterization of Preceramic Inks for Direct Ink Writing of Ceramic Matrix Composite Structures

Investigating the effect of polymer additives on the rheology of SiC/clay paste for use in Direct Ink Writing method

UV-assisted direct ink writing of Si3N4/SiC preceramic polymer suspensions

SiCw/SiCp Reinforced 3D-Sic Ceramics Using Direct Ink Writing of Polycarbosilane-Based Solution: Microstructure, Composition and Mechanical Properties

Preparation and Mechanical Performance of SiCw/geopolymer Composites Through Direct Ink Writing

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Development and Characterizations of Novel Aqueous-Based Ceramic Inks for Inkjet Printing

Effect of solid loading on properties of zirconia ceramic by direct ink writing

Direct Ink Writing of Special-Shaped Structures Based on Tio2 Inks

Preparation and Characterization of Neodymium Disilicate Ceramic Ink by Mechanical Grinding

Additive manufacturing of SiC-Sialon refractory with excellent properties by direct ink writing

Direct ink writing of zirconia three-dimensional structures

3D printing Si3N4-bonded SiC refractories fabricated using colloidal films-containing slurries based on non-spherical SiC and Si powders

Rheology of organics-free aqueous ceramic suspensions for additive manufacturing of dense silicon nitride ceramics

On the cogent formulation of an elastomeric silicone ink material for direct ink write (DIW) 3D printing