Abstract:Successful preparation of photopolymerizable ceramic slurries using non-oxide ceramics and their 3D printing is highly challenging as the ceramic powders often possess high UV-light absorbance. Even though pre-oxidation of the powders could improve the slurry printability, the residual oxygen element in the material would eventually deteriorate the material purity and performance. In this study, a separated redox route (pre-oxidation, 3D printing and carbothermal reduction) was proposed to overcome these challenges. SiC ceramic powder was pre-oxidized into SiC@SiO2 core-shell form to lower the UV-light absorbance. It was found that the ultraviolet (UV) light absorbance value of SiC powder at 405 nm decreased 20% from 0.357 to 0.284 after pre-oxidation process. The UV-light penetration depth of SiC@SiO2 ceramic slurries at 40 similar to 55 vol% solid loading ranging from 14.81 to 12.82 mu m, which surpassed two times that for 40 vol% raw SiC ceramic slurry. Different-shaped structures of SiC@SiO2/resin green ceramic bodies were successfully fabricated by vat photopolymerization 3D printing. The oxygen element resided was then eliminated by carbothermal reduction to avoid detriment of SiO2 to the mechanical performance of the SiC ceramics. Phenolic epoxy acrylate resin with 14 wt% pyrolytic carbon (PyC) yield was chosen as the carbon source and thus the SiC@SiO2/resin green body pyrolyzed into SiC@SiO2/PyC ceramics after 1200 degrees C. It was found that after the heating temperature was further raised to 1600 degrees C, most of the pre-introduced SiO2 shells on the surface of SiC particles were in situ transformed into SiC nanowires through carbothermal reduction reaction between SiO2 and PyC, and the content of oxygen element in the ceramic matrix sharply dropped from 20.21% to 2.08%. The results demonstrated that through the proposed redox route, the photopolymerization-related issues including high UV-light absorbance and pre-oxidation-induced impurity for 3D printing of SiC ceramic slurries can be tackled. Finally, high purity porous SiCnw/SiC ceramic components with different structures were produced. This study provides a promising route for the preparation and 3D printing of photopolymerization ceramic slurries using non-oxide ceramics possessing high UV-light absorbance.

SiCw/SiCp Reinforced 3D-Sic Ceramics Using Direct Ink Writing of Polycarbosilane-Based Solution: Microstructure, Composition and Mechanical Properties

3D Printing of SiC Ceramic: Direct Ink Writing with a Solution of Preceramic Polymers

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Optimized preceramic polymer for 3D structured ceramics via fused deposition modeling

3D Printing and in Situ Transformation of SiCnw/SiC Structures

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Digital Light Processing of Si-based Composite Ceramics and Bulk Silica Ceramics from a High Solid Loading Polysiloxane/sio2 Slurry

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Direct Ink Writing of Chopped Carbon Fibers Reinforced Polymer-derived SiC Composites with Low shrinkage and High Strength

Lattice-structured SiC ceramics obtained via 3D printing, gel casting, and gaseous silicon infiltration sintering

Investigation of curing behavior and mechanical properties of SiC ceramics prepared by vat photopolymerization combined with pressureless liquid-phase sintering using Al 2 O 3 -coated SiC powder

Investigation of Curing Behavior and Mechanical Properties of SiC Ceramics Prepared by Vat Photopolymerization Combined with Pressureless Liquid-Phase Sintering Using Al2O3-coated SiC Powder

Microstructure, thermal, and mechanical properties of hierarchical porous silicon carbide made by direct ink writing

3D SiC Containing Uniformly Dispersed, Aligned SiC Whiskers: Printability, Microstructure and Mechanical Properties

Three-dimensional printing of SiCN ceramic matrix composites from preceramic polysilazane by digital light processing

Stereolithography of SiOC Polymer‐Derived Ceramics Filled with SiC Micronwhiskers

PREPARATION OF 3D-Cf/SiC COMPOSITE WITH LOW-MOLECULAR POLYCARBOSILANE

3D-printing of polymer‐derived SiCN ceramic matrix composites by digital light processing

Preparation And Properties Of Sic Ceramics Via Sls/Cip Process

Fabrication of SiC Ceramic Architectures Using Stereolithography Combined with Precursor Infiltration and Pyrolysis

Preparation and properties of SiC ceramics <i>via</i> SLS/CIP process