Abstract:The realization of the necessary energy-efficient technological solutions for the production of highly porous SiC-ceramic materials requires appropriate research. The results of developing energy-efficient one-step methods for the synthesis of porous SiC-based ceramics and studying the characteristics of the obtained ceramics are presented. The effect of the morphology of initial powders on the synthesized product is considered. Ultrafine silicon carbide powders of two types, identical in characteristic particle size, but quite different in the surface morphology, were used as fillers in the synthesis of experimental samples of porous ceramics. The first one was obtained by the traditional furnace method (SiC f ), the second one was synthesized by the technology of self-propagating high-temperature synthesis (SiC shs ). It is shown that the particle morphology of initial powder components determines the structural parameters and characteristics of synthesized porous ceramics. The pore space parameters (average pore size, specific surface area, equivalent hydraulic diameter, permeability, etc.) can vary significantly. Porous ceramic materials synthesized on the basis of SiC f have an open porosity of 47%, high liquid permeability (up to 2 mDarcy), overwhelming dominance of α-SiC phase, and a narrow pore distribution with an average pore size of about 1 μm. High open porosity (more than 58 %), highly developed nanostructured pore space surface with an area of more than 12 m 2 /g, and wider pore size distribution (average pore size — 140 nm) are observed in porous ceramic materials based on SiC shs . The obtained results can be used to improve energy-efficient synthesis technologies and methods for predicting the properties of highly porous SiC-based ceramic materials. This will make it possible to create highly porous SiC ceramics within a priory predicted limits of effective applicability for the processes of ultrafiltration or catalysis.

Microstructure, thermal, and mechanical properties of hierarchical porous silicon carbide made by direct ink writing

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Three‐dimensional (3D) flexible nanofibrous network knitting on hierarchical porous architecture

Direct Ink Writing of Chopped Carbon Fibers Reinforced Polymer-derived SiC Composites with Low shrinkage and High Strength

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Advanced hierarchical biomorphous silicon carbide monoliths

Geometrically Complex Silicon Carbide Structures Fabricated by Robocasting

3D printing of porous SiC ceramics added with SiO2 hollow microspheres

Preparation of Hierarchical Porous Silicon Carbide Monoliths via Ambient Pressure Drying Sol–Gel Process Followed by High-Temperature Pyrolysis

Direct Vat‐Photopolymerization 3D Printing of Hierarchically Porous SiC Loaded with Co/Ni Based Catalysts by Using Pickering Emulsions

Building SiC-based composites from polycarbosilane-derived 3D-SiC scaffolds via polymer impregnation and pyrolysis (PIP)

Study of the effect of the morphology of initial powders on the structural and dimensional characteristics of SiC-based porous ceramic materials

Binder jetting additive manufacturing of hierarchical structural SiC w /SiC composites

3D-Printed Electrically Conductive Silicon Carbide

3D Printing of Hollow Microspheres into Strong Hierarchical Porous Ceramics

Effect of particle size on additive manufacturing of complex architecture of silicon carbide

Controllable reduction of absorbance and two-step reaction for 3D-printed SiC ceramics with micron-level periodic structure

Direct ink writing of hierarchically porous Al 2 O 3 matrix composites with enhanced wettability of Al

Structure design influencing the mechanical performance of 3D printing porous ceramics