Abstract:The wettabilities of molten metals on ceramics are poor normally. In order to improve the wettability, all existing ceramic brazing methods introduce a compound transition layer that is formed by the reaction of active metal and ceramic. The transition layer between brazing seam and ceramic however creates negative effect on the properties of brazing joints. This paper reports our study of the wetting effect of sputtered Al particles on AlN, which enables the direct brazing of AlN using deposited Al-based films as fillers, thereby eliminating the need of a transition layer. The results show that under the bombardment of energetic sputtered Al particles, Al-N chemical bonding is formed at the interface between Al film and AlN, which typically requires temperatures above 850 ℃, much higher than the melting point of Al. The bonding remained intact even after the Al film has been melted, achieving the wetting effect on AlN. As a result, the direct brazing of AlN without the need of a transition layer becomes feasible. The shear strength of Al/AlN joint using this process reaches 104 MPa. The addition of 3.8 at.% Cu to film fillers increases the shear strength to 165 MPa. The fracture is generated in metallic brazing seam in both cases. When Cu content increases to 9.1 at.%, the segregation of Cu at the interface between the brazing seam and the ceramic reduces the shear strength of the joint to 95 MPa. With Al-20 at.% Ge, the brazing temperature can be lowered to 510 ℃, although the segregation of Ge at interface results in a low shear strength of 48 MPa. Instead of the traditional use of molten metals, utilization of the metallic vapor particles to bombard AlN achieves the wetting and the direct brazing of ceramics, with no negative effect of transition layers. This breakthrough method provides a brand new perspective to the technique of ceramic brazing.

Direct ink writing of hierarchically porous Al 2 O 3 matrix composites with enhanced wettability of Al

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Effect of Al(OH)3 addition on the properties of SiC/Al2O3 composite porous ceramics

Direct ink writing additive manufacturing of porous alumina-based ceramic cores modified with nanosized MgO

Effect of Al(OH)<sub>3</sub> Addition on the Properties of SiC/Al<sub>2</sub>O<sub>3</sub> Composite Porous Ceramics

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Optimization of the sintering thermal treatment and the ceramic ink used in direct ink writing of α-Al2O3: Characterization and catalytic application

A novel composite binder design for direct ink writing alumina-based ceramics with enhanced strength at low sintering temperature

Effect of Different Aluminum Sources on the Preparation and Properties of SiC/Cordierite Composite Porous Ceramics

Enhancement of Wettability of Aluminum Based Silicon Carbide Reinforced Particulate Metal Matrix Composite

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Microstructure, thermal, and mechanical properties of hierarchical porous silicon carbide made by direct ink writing

INFLUENCE OF Al2O3 ON PREPARING POROUS SILICON NITRIDE BASED CERAMIC FROM RICE HUSK

Fabrication and Properties of SiC/mullite Composite Porous Ceramics

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Microstructure and Mechanical Properties of Unidirectional, Laminated Cf/SiC Composites with α-Al2O3 Nanoparticles as Filler

"Wetting" and Brazing of Aln by Sputtered Al

Direct Ink Writing of Porous Cordierite Honeycomb Ceramic

Interfacial Modification and Performance Enhancement of Carbon Matrix/aluminum Composites