Abstract:Ceramic-based porous structures have received considerable attention due to their excellent thermal properties. However, the disordered pore arrangement inside traditional porous ceramics would significantly weaken their structural performance. This paper presents the vat photopolymerization of polymer-derived ceramics (PDCs) to fabricate porous SiC ceramic components with triply period minimal surface (TPMS), which have a regular pore arrangement and can be used as catalyst supports for hydrogen production. The photosensitive preceramic polymer resin with low viscosity was prepared by directly dissolving polycarbosilane (PCS) into photosensitive resin and organic solvent. Five different types of TPMS structures, including the P, G, D, I-WP, and F-RD surfaces, were designed and printed using the optimized preceramic polymer resin. After the ceramization process, the TPMS structural SiC ceramic components with a high porosity of 80% were successfully obtained, exhibiting precise microstructures and excellent mechanical properties . Furthermore, the fabricated TPMS structural SiC components were used as catalyst supports in a methanol steam reforming (MSR) microreactor, and the experimental results show that the TPMS structural catalyst support is a great choice for hydrogen production. Notably, catalyst supports with P, G, and D surfaces showed excellent flow performance with different flow paths. The D surface, in particular, exhibited the best reaction performance with the hydrogen production and conversion rate of 82.62 ml/min and 78.7%.

Direct Ink Writing of Porous Cordierite Honeycomb Ceramic

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Direct ink writing of Pd-Decorated Al<sub>2</sub>O<sub>3</sub> ceramic based catalytic reduction continuous flow reactor

Direct ink writing of hierarchically porous Al 2 O 3 matrix composites with enhanced wettability of Al

Diatomite-based porous ceramics with high apparent porosity: Pore structure modification using calcium carbonate

Fabrication of Porous Ceramics by Direct Foaming

3D printing of open-porous cellular ceramics with high specific strength

Direct ink writing additive manufacturing of porous alumina-based ceramic cores modified with nanosized MgO

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

3D Printing of Hollow Microspheres into Strong Hierarchical Porous Ceramics

Microstructure, thermal, and mechanical properties of hierarchical porous silicon carbide made by direct ink writing

Preparation and Pore Structure Characteristics of SiC Honeycomb Ceramics with Macroporous Walls

Preparation and photocatalytic properties of macroporous honeycomb alumina ceramics used for water purification

Fabrication and properties of diatomite ceramics with hierarchical pores based on direct stereolithography

Effect of starch pore formers with different particle sizes on cordierite porous ceramics

Fabrication and Characterization of Hierarchically Macroporous Al2O3 Ceramic Supported ZnO/ZnS Photocatalyst

Novel ceramic supports for catalyst with hierarchical pore structures fabricated via additive manufacturing-direct ink writing

Near Net Shape Fabrication of Porous Cordierite by Combination of Foam Gel‐casting and Freeze‐drying

Vat photopolymerization of polymer-derived SiC ceramic with triply period minimal surface structure for hydrogen production

Porous Mullite Ceramics with Hierarchical Pores Constructed Via Vat Photopolymerization of Multi-Phase Pickering Emulsion

Preparation and characteristics of honeycomb mullite ceramics with controllable structure by stereolithography 3D printing and in-situ synthesis