Abstract:For improving the wear resistance of Al-30Si-5Cu coating, in this study, the composite coating in-situ synthesized TiC-TiN-TiN 0.8 C 0.2 /Al-30Si-5Cu (TiCN/Al-30Si-5Cu) was prepared used TiH 2 -graphite aggregates as raw materials and plasma spraying technology. The effect of in-situ synthesized ceramic reinforcements on the coating was researched in detail. The results showed that during the plasma spraying process, TiH 2 decomposed and chemically reacted with graphite to form TiC. Additionally, some Ti also reacted with N 2 and O 2 in the air to form TiN and TiO 2 . The phases composition of TiCN/Al-30Si-5Cu composite coating were α-Al, β-Si, θ-Al 2 Cu, β-Ti, TiC, TiN, TiN 0.8 C 0.2 , TiO 2 , as well as amorphous CN X and residual graphite. The TiC-dominated ceramic phases and β-Si were uniformly distributed in the coating, which were tightly bound to the α-Al matrix. Because of the exceptionally rapid cooling rate during the coating preparation, a minor amount of submicron Si particles were also generated. The microhardness, elasticity modulus, and fracture toughness of TiCN/Al-30Si-5Cu composite coating appeared improvements compared to those of Al-30Si-5Cu coating. The TiCN/Al-30Si-5Cu composite coating exhibited smoother friction coefficient curve, along with lower friction coefficient and wear volume in comparison to the Al-30Si-5Cu coating. This suggested that the ceramic reinforcing phases in-situ synthesized led to a notable advancement in the wear resistance of the TiCN/Al-30Si-5Cu composite coating. The wear resistance of TiCN/Al-30Si-5Cu composite coating demonstrated an increasement of 78.3 % over the substrate and 28.2 % over the Al-30Si-5Cu coating. Under the dry friction test conditions outlined in this study, the wear mechanism of the TiCN/Al-30Si-5Cu composite coating included abrasive wear and fatigue wear, coupling with a minimal amount of oxidative wear.

Microstructure and Properties of In-Situ Crb2-Cr3c2-Al2o3 Composite Coating Prepared by Plasma Spraying

The Microstructure of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Microstructure and properties of CrB2-Cr3C2 composite coatings prepared by plasma spraying

Microstructure, formation mechanism and properties of plasma-sprayed Cr7C3—CrSi2—Al2O3 coatings

Microstructure and properties of in-situ ZrB2-ZrC composite coatings by plasma spraying

Microstructure characterization of in-situ ZrC composite coating with graceful toughness and improved tribological properties prepared by plasma spraying

TEM characterization and toughening mechanism of in-situ NbB2-NbC-Al2O3 composite coatings prepared by plasma spraying

TiC-TiSi2-Al2O3 composite coatings prepared by spray drying, heat treatment and plasma spraying

Microstructure and properties of Cr7C3-CrSi2 composite coatings prepared by plasma spraying

In-situ synthesis, microstructure, and properties of NbB2-NbC-Al2O3 composite coatings by plasma spraying

Friction and wear characteristics of in-situ Cr+(Cr,Al)2O3 composite coating fabricated by plasma spraying

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Effect of nano‐Al 2 O 3 on the microstructure and properties of NbB 2 ‐NbC composite coatings prepared by plasma spraying

Microstructure and properties of niobium carbide composite coatings prepared by plasma spraying

Fundamental understanding on the microstructure and corrosion resistance of Cr-(Cr, Al)2O3 composite coatings in-situ synthetized by reactive plasma spraying

Toughening mechanism of in-situ synthesized ZrB2 based composite coating by plasma spraying

Properties of Reactive Plasma Sprayed Tib2-Tic0.3n0.7 Based Composite Coatings with Cr Addition and Laser Surface Treatment

Microstructure of plasma-sprayed Al2O3-ZrO 2 composite coatings

In-situ TiC-Ti5Si3-SiC composite coatings prepared by plasma spraying

Enhanced Interfacial Bonding and Superior Oxidation Resistance of CoCrAlY-TiB2 Composite Coating Fabricated by Air Plasma Spraying

Microstructure and tribological properties of Al-30Si-5Cu composite coating reinforced with ceramic phases synthesized in situ by plasma spraying