Abstract:The corrosion resistance and stress corrosion cracking (SCC) susceptibility of Type 347H stainless steel (SS) in supercritical water (SCW) were investigated. The general corrosion behavior was investigated by exposure test and the specimens after testing were characterized utilizing scanning electron microscopy (SEM), Auger and x-ray diffraction analysis, optical microscopy, and energy dispersive spectroscopy (EDS). The results show that with the increase of testing temperature, the corrosion rate of the materials is greatly enhanced. The corrosion process is analyzed and the formation of oxide islands on the surface of the corroded sample is attributed to the higher diffusion rate of Cr along the grain boundary. The effects of temperature and dissolved oxygen on SCC susceptibility were investigated by slow strain rate tensile test. The fractographs were characterized by SEM and the cross-section morphologies were characterized with back-scattered electron imaging, SEM, and EDS. The results indicate that, as temperature is increased, the tensile strength and strain of materials is greatly reduced, while the oxygen content in SCW has a limited effect on the mechanical properties. Intergranular cracking and ductile fracture are the main fracture modes for Type 347H SS tested in SCW, independent of temperature and oxygen content. The implications of the results to the mechanisms of SCC are discussed.

Investigations on the SCC initiation behavior of cold worked 316 L in high temperature oxygenated water at constant loads

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Insights into the Stress Corrosion Cracking Propagation Behavior of Alloy 690 and 316 L Stainless Steel in KOH Versus LiOH Oxygenated Water

Determining SCC resistance of stainless steel claddings in high- temperature water by constant load crack growth tests and slow strain rate tests

Combined effects of machining-induced residual stress and external load on SCC initiation and early propagation of 316 stainless steel in high temperature high pressure water

Stress Corrosion Crack Growth Behavior of Type 310S Stainless Steel in Supercritical Water

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

A Research on the Corrosion and Stress Corrosion Cracking Susceptibility of 316L Stainless Steel Exposed to Supercritical Water

Stress Corrosion Cracking of 316l Haz for 316l Stainless Steel/Inconel 52m Dissimilar Metal Weld Joint in Simulated Primary Water

Stress Corrosion Cracking of Uni-Directionally Cold Worked 316ng Stainless Steel in Simulated Pwr Primary Water with Various Dissolved Hydrogen Concentrations

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Evaluation of Stress Corrosion Cracking Susceptibility of Forged 316 Stainless Steel in Simulated Primary Water

Stress Corrosion Cracking Behavior of Cold-Drawn 316 Austenitic Stainless Steels in Simulated Pwr Environment

Effect of Cold Work Level on the Crack Propagation Behaviour of 316LN Stainless Steel in High-Temperature Pressurized Water

Quantitatively evaluating the contribution of intergranular carbides, Cr-depleted zone, and grain boundary to intergranular stress corrosion cracking of Alloy 600 in a simulated boiling water reactors environment with high oxygen concentrations

Crack Initiation Mechanisms for Low Cycle Fatigue of Type 316ti Stainless Steel in High Temperature Water

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Stress Corrosion Cracking of Fusion Boundary for 316L/52M Dissimilar Metal Weld Joints in Borated and Lithiated High Temperature Water

Investigation of stress corrosion cracking behavior and mechanism analysis of a 1900 MPa-grade ultra-high-strength stainless steel

Corrosion and Stress Corrosion Cracking Susceptibility of Type 347H Stainless Steel in Supercritical Water