Abstract:Stress corrosion cracking (SCC) of 316L single-crystal austenitic stainless steel subjected to low loads (σnom = 20-40 MPa) in a 45 % boiling MgCl2 solution was studied using synchrotron X-ray computed tomography, finite element analysis and so on. Results show that there was no surface slip band around the nucleation sites and the tips of short cracks. Three-dimensional reconstruction of discontinuous zig-zag surface SCC crack indicates that the crack was continuous inside the specimen. The obtaining through two-surface trace analysis manifests, rather than {1 1 1} slip planes, the cracks extended along {1 0 0} planes with the lowest surface energy. It is considered that microcleavage and local dissolution synergistically led to the SCC advance, and microshear was also one of the primarily microscopic SCC mechanisms under the high load. The three-dimensional SCC model was created at the low stress level, where a main SCC crack grew along the MPD due to anodic dissolution, and a microdefect was formed on the crack front. When the microdefect enlarged to a critical size, secondary microcracks nucleated at the stress-concentrated microdefect shoulders. Then, the microcracks propagated to two sides of the MPD through anodic dissolution, microcleavage or mciroshear, resulting in the formation of the river-like fractography and the discontinuous surface SCC cracks with or without surface slipping.

Stress Corrosion Cracking at Low Loads: Surface Slip and Crystallographic Analysis

A Three-Dimensional Model of Non-Slipping Stress Corrosion Cracking under Low Loads

An Investigation of Corrosion-Induced Stress During SCC

Stress corrosion cracking of TC4 ELI alloy with different microstructure in 3.5% NaCl solution

Characteristic of Acoustic Emission Signal from Stress Corrosion Cracking in Low-Carbon Nitrogen-Enhanced Stainless Steel

Investigations on the SCC initiation behavior of cold worked 316 L in high temperature oxygenated water at constant loads

Comprehensive Impact of Machined Surface Integrity on Stress Corrosion Cracking Initiation in 316 Austenitic Stainless Steel

Correlation between machining-induced surface alterations and stress corrosion cracking susceptibility of au stenitic stainless steels

Experimental Study of Micro-Cracks in Stress Corrosion of Fiber Reinforced Composites

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads

Observations of Stress Corrosion Cracking in Pipeline Steel in Corrosive Seawater Environment Including Detailed Observation of the Crack Initiation Mechanism

Stress Corrosion Cracking Behavior of Cold-Drawn 316 Austenitic Stainless Steels in Simulated Pwr Environment

Observation of Dislocation Microstructures and Simulation of Stress Field During Fatigue Crack Initiation in a Copper Single Crystal

Fractography of Stress Corrosion Cracking of 20% Cold Worked Type 304 H Stainless Steel Containing δ-Ferrite in Oxidizing Primary Water

Crystallographic effects on transgranular chloride-induced stress corrosion crack propagation of arc welded austenitic stainless steel

Simulation of Internal~ Stresses~ Near the Surface and Fatigue Crack Nucleation for A Copper Single Crystal in Cyclic Deformation Saturation Stage

In-situ analysis of SCC initiation on Alloy 600 surface in primary water environment using digital image correlation with electron backscatter diffraction

Effect of Static Mechanical Load on Intergranular Stress-Corrosion Cracking of 7050-T7451 C-Ring Specimens

The Effects of Grain Boundary Carbide Density and Strain Rate on the Stress Corrosion Cracking Behavior of Cold Rolled Alloy 690

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Effect of surface nanocrystallization induced by mechanical grinding treatment on stress corrosion cracking behavior of 316 L austenitic stainless steel in boiling MgCl 2 solution