Dual Functions of Three-Dimensional Hierarchical Architecture on Improving the Rate Capability and Cycle Performance of LiNi0.8Co0.1Mn0.1O2 Cathode Material for Lithium-Ion Battery

Wenchao Liu,Yunhao Zang,Jiangying Qu,Feng Gao,Shahid Zaman,Gang Zhou,Shaomin Ji

DOI: https://doi.org/10.1016/j.ceramint.2021.12.097

IF: 5.532

2021-01-01

Ceramics International

Abstract:The main obstacles in lithium-ion battery are limited by rate performance and the rapid capacity fading of LiNi0.8Co0.1Mn0.1O2 (NCM811). Herein, a novel three-dimensional (3D) hierarchical coating material has been fabricated by in situ growing carbon nanotubes (CNTs) on the surfaces of Ni-Al double oxide (Ni-Al-LDO) sheets (named as LDO & CNT) with Ni-Al double hydroxide (Ni-Al-LDH) as both the substrate and catalyst precursor. The resultant LDO & CNT nanocomposites are uniformly coated on the surfaces of NCM811 by the physical mixing method. The rate capability of the resultant cathode material retains to 78.80% at a current rate of 3C. Its capacity retention increases by 6.7-14.42% compared with pristine NCM811 after 100 cycles within a potential range of 2.75-4.3 V at 0.5C. The improved rate capability and cycle performance of NCM811 are assigned to the synergistic effects between Ni-Al-LDO and CNTs. The hierarchical LDO & CNT nanocomposites coating on the surface of NCM811 avoids the aggregation of conductive CNTs and the stacking of Ni-Al-LDO nanosheets. Furthermore, it accelerates Li+ and electrons shuttle and reduces the reaction of Li2O with H2O and CO2 in air, which results in Li2CO3 and LiOH alkali formation on the NCM811 surface.