Non-isothermal Aging: A Heat Treatment Method That Simultaneously Improves the Mechanical Properties and Corrosion Resistance of Ultra-High Strength Al-Zn-Mg-Cu Alloy
Weiyi Wang,Qinglin Pan,Xiangdong Wang,Yuanwei Sun,Ji Ye,Geng Lin,Shuhui Liu,Zhiqi Huang,Shengqian Xiang,Xiaoping Wang,Yaru Liu
DOI: https://doi.org/10.1016/j.jallcom.2020.156286
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:In ultra-high strength Al-Zn-Mg-Cu alloys, traditional heat treatments such as peak aging, two-stage aging and retrogression and re-aging cannot perfectly balance the relationship between mechanical properties and corrosion resistance and usually consume more time. Based on previous studies, the aim of this paper is to establish a suitable non-isothermal aging method for ultra-high strength Al-Zn-Mg-Cu alloys. In this study, after enhanced solution treatment and aging process with the heating rate of 20 degrees C/h, the alloy achieves excellent hardness and ultimate tensile strength of 195.7 HV and 680 MPA, respectively. When heating rate increases to 40 degrees C/h, non-isothermal aging can also ensure the alloy achieve the excellent mechanical properties (195.6 HV, 675 MPA). Similar to mechanical properties, the samples have outstanding resistance to intergranular and exfoliation corrosion, which is in accordance with the results of potentiodynamic polarization and electrochemical impedance spectroscopy tests. Evidences from high resolution transmission electron microscopy show that non-isothermal aging can promote the formation of a large number of smaller GP zones, eta' precipitates and few eta(2) precipitates inside grains, which greatly strengthens the mechanical properties. Furthermore, the grain boundaries precipitates transform from continuous to discontinuous and precipitate free zones form gradually, which greatly enhances the corrosion resistance. Because of these precipitates inside grains and grain boundaries, the samples with enhanced solution treatment +20 degrees C/h aging process and both solution treatments +40 degrees C/h aging process can achieve good mechanical properties closing to T6 state and corrosion resistance similar to T74 state simultaneously with much less aging time. (C) 2020 Elsevier B.V. All rights reserved.