Effect of post-heat treatment on the microstructure, mechanical, and corrosion properties of laser powder bed fused Al–Zn–Mg–Cu–Si–Zr–Er alloys
Zhiqian Zhang,Dehua Li,Shengci Li,Hui Tang,Yu Zhang,Tingting Dong,Weirong Li,Yanfang Li,Olanrewaju A. Ojo
DOI: https://doi.org/10.1016/j.jmrt.2023.10.009
IF: 6.267
2023-10-15
Journal of Materials Research and Technology
Abstract:Three different post-heat treatments, including direct aging (DA), solution heat treatment + precipitate hardening (T6), and retrogression and re-ageing (RRA), were carried out on a Si–Zr–Er modified Al–Zn–Mg–Cu alloy, which is manufactured by laser powder bed fusion (LPBF). The results show that direct aging maintains the cellular structure of the as-printed (AP) alloy, while T6 and RRA promoted the damage and decomposition of the cellular structure. The size of the primary Al 3 (Er,Zr) phase increased after heat treatment, and secondary Al 3 (Er,Zr) phases were uniformly distributed in the matrix with a size of 5–20 nm. The Mg 2 Si phase in the DA alloy was a long strip pattern, but uniformly distributed in the T6 and RRA alloy. The ultimate tensile strength of the AP, DA, T6, and RRA alloys reached 468, 474, 389, and 354 MPa, respectively. The size, shape, and distribution of the Al 3 (Er,Zr) and Mg 2 Si phases have a significant impact on their corrosion resistance, with the latter having a stronger effect. To sum up, the strength of the DA alloy is increased, but its corrosion performance is decreased with heat treatment. On the other hand, the strength of the T6 and RRA alloys is somewhat sacrificed, but their plasticity and corrosion resistance are significantly enhanced.
materials science, multidisciplinary,metallurgy & metallurgical engineering