Abstract:One of the critical challenges for the protonic ceramic fuel cell stack is sealing electrolytes and interconnects. However, the traditional Ag-CuO sealant will aggravate the oxidation along the intercon-nect surface and result in brittle compound layers at the BaZr0.1Ce0.7Y0.1Yb0.1O3-delta (BZCYYb) electrolyte interface. The present work demonstrates that a silver particle interlayer with high dislocation density can be adopted to join BZCYYb electrolyte to the interconnect (AISI 441 stainless) in air instead of traditional Ag-CuO sealant. Elevating temperatures result in a sufficient bonding at the Ag/BZCYYb interface, and a defect-free joint is obtained at 950 degrees C. Atomic bonding at Ag/BZCYYb interface is confirmed by TEM. Also, a dense and thin oxide layer (2-3 mm) is formed along the AISI 441 interface. Ag particles in the interlayer provide the main driving force for the sintering joining. The massive dislocations promote the recovery and recrystallization of the Ag interlayer, as well as the interdiffusion of BZCYYb/Ag. After aging in the wet oxidizing atmosphere at 600 degrees C for 300 h, joints remain intact and dense, indicating superior oxidation resistance and aging performance. Besides, the joint shear strength (25.3 MPa) is 59 % higher than that of the joint brazed by traditional Ag-CuO. (C) 2022 The Chinese Ceramic Society. Production and hosting by Elsevier B.V.

Joining of Co coated ferritic stainless steel to ceramic solid oxide cells by a novel Ag-SiO<sub>2</sub> braze

Ag–SiO2 - an Optimized Braze for Robust Joining of Commercial Coated Stainless Steel to Ceramic Solid Oxide Cells

Microstructure Evolution and Mechanical Properties of Co Coated AISI 441 Ferritic Stainless Steel/ysz Reactive Air Brazed Joint

Enhancing the Long-Term Stability of Ag Based Seals for Solid Oxide Fuel/electrolysis Applications by Simple Interconnect Aluminization

Joining 3YSZ Electrolyte to AISI 441 Interconnect Using the Ag Particle Interlayer: Enhanced Mechanical and Aging Properties

Joining YSZ Electrolyte to AISI 441 Interconnect for Solid Oxide Cells Using the Ag Interlayer: Enhanced Mechanical and Aging Properties

Electrochemically enhanced wetting of 3YSZ and Mn1.5Co1.5O4 by Ag−CuO and their application in flash joining

Reactive Air Brazing of the YSZ/AISI 310s Couples Using a Novel Ag–Nb2O5 Sealant

Joining of Solid Oxide Fuel/electrolysis Cells at Low Temperature: A Novel Method to Obtain High Strength Seals Already at 300 °C

Oxidation Behavior of Ferritic Stainless Steel Interconnect Coated by a Simple Diffusion Bonded Cobalt Protective Layer for Solid Oxide Fuel Cells

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Joining The Bazr0.1ce0.7y0.1yb0.1o3-Delta Electrolyte To Aisi 441 Interconnect For Protonic Ceramic Fuel Cell Applications: Interfacial Microstructure And Long-Term Stability

Brazing of SiC Ceramics Pretreated by Chromium Coating Using Inactive AgCu Filler Metal

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Brazing of SiC ceramic to Al<sub>0.3</sub>CoCrFeNi high entropy alloy by graphene nanoplates reinforced AgCuTi composite fillers

Joining of SiO2 Ceramic and TC4 Alloy by Nanoparticles Modified Brazing Filler Metal

Joining of Yttria Stabilised Zirconia to Ti6Al4V Alloy Using Novel CuO Nanostructure Reinforced Cu Foam Interlayer

A Novel Ag–CuAlO2 Sealant for Reactive Air Brazing of 3YSZ and AISI 310S

Silver Particle Interlayer with High Dislocation Density for Improving the Joining of BaZr0.1Ce0.7Y0.1Yb0.1O3-δ Electrolyte and AISI 441 Interconnect

Efficient FeCoNi/CeO 2 coatings for solid oxide fuel cell steel interconnect applications