Abstract:AISI 430 stainless steel is used for interconnects in solid oxide fuel cells (SOFCs). One of the main problems with this steel is the formation of chromia scales during oxidation at high temperature and thus increasing electrical resistance. In order to solve such problems, a protective and conductive coating layer can be applied on interconnects. In this study, AISI 430 steel was coated by Ni–P–TiO2–ZrO2 composite coating. To evaluate the oxidation behavior, isothermal and cyclic oxidation tests were used at 800 °C. Area specific resistances (ASR) of uncoated and coated samples were also compared as a function of time during oxidation at 800 °C. Chemical composition and surface morphology of the samples were examined before and after oxidation by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). In isothermal and cyclic oxidation tests, coated samples showed lower weight gain due to the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel. This spinel prevented outward Cr diffusion, and improved the oxidation resistance of the AISI 430 stainless steel substrate. The obtained result by cyclic oxidation revealed that the coated substrates were resistant against cracking and spallation. Also, the results showed that the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel and also the presence of TiO2 and ZrO2 caused ASR reduction. ASR of Ni–P–TiO2–ZrO2-coated specimens after 300 h of oxidation at 800 ºC (14.21 mΩ cm2) was lower than the uncoated specimens (41.84 mΩ m2) after the same time of oxidation.

Application of sol–gel technique to synthesis of copper–cobalt spinel on the ferritic stainless steel used for solid oxide fuel cell interconnects

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Efficient FeCoNi/CeO 2 coatings for solid oxide fuel cell steel interconnect applications

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Cu and Y doped (Co, Mn)3O4 spinel coatings on Crofer ferritic alloy by composite electrodeposition

Iron doped manganese cobaltite spinel coatings produced by electrophoretic co-deposition on interconnects for solid oxide cells: Microstructural and electrical characterization

Review—(Mn,Co)3O4-Based Spinels for SOFC Interconnect Coating Application

CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels as efficient protective coating layers on SUS430 for SOFC interconnect

Highly dense (Mn,Co)3O4 spinel protective coating derived from Mn–Co metal precursors for SOFC interconnect applications

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Performance and In-Situ Densification of Mn-Co Spinel Coating on SUS430/441 Interconnect by Spraying Method

Influences of Composite Electrodeposition Parameters on the Properties of Ni-Doped Co-Mn Composite Spinel Coatings

Fabrication of Mn–Co Alloys Electrodeposited on AISI 430 Ferritic Stainless Steel for SOFC Interconnect Applications

Thermal Growth and Performance of Manganese Cobaltite Spinel Protection Layers on Ferritic Stainless Steel SOFC Interconnects

Oxidation and electrical behavior of AISI 430 steel coated with Ni–P–TiO2–ZrO2 composite for SOFC interconnect application

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

Highly Conductive Mn-Co Spinel Powder Prepared by Cu-Doping Used for Interconnect Protection of SOFC