Abstract:MnCo2O4 spinel coating is considered as one of the most promising protective coatings on the surface of ferritic stainless steel interconnects in solid oxide fuel cells (SOFCs). And the doping of metallic elements and active rare earth elements may further improve the electrical conductivity and antioxidant properties of spinel coatings. In this work we firstly prepare the Cu-doped and Ce-doped MnCo2O4 spinel coatings (abbreviated as MCCu, MCCe) on the surface of SUS430 substrate by Sol-Gel and electrophoretic deposition methods. The optimal doped ratio of Cu and Ce based on the results of oxidized mass gain and area-specific resistance (ASR) tests are determined respectively. Then we deposit Cu-Ce co-doped MnCo2O4 spinel coatings (abbreviated as MCCuCe) accordingly. The successful deposition of the target modified spinel coating on the substrate surface is confirmed using SEM-EDS, XRD, XPS characterization. The performance test results of the MCCuCe coating on the SUS430 surface show that the mass gain after 500 h oxidation at 800 degrees C in air is 1.3564 x 10(-3) mg cm(-2), and the ASR at 800 degrees C after 500 h oxidation is 9.80m Omega cm(2), which is much lower than those of the bare SUS430 substrate and the substrate with deposited MnCo2O4 spinel coating. And the MCCuCe protective coating plays a better role in preventing the diffusion of Cr from the substrate. Further analysis prove that the doping Cu mainly contributes to the electrical conductivity and adhesion to the substrate while the doping Ce mainly improve the anti-oxidation and Cr diffusion resistance. This work determines the optimal doped ratio of Cu and Ce and provides a simple way to prepare the Cu-Ce co-doped MnCo2O4 spinel coatings on the ferritic interconnects, which effectively improve comprehensive performances of MnCo2O4 spinel coatings and helps to accelerate the industrial application of SUS430 ferrite in the SOFCs.

Cu and Y doped (Co, Mn)3O4 spinel coatings on Crofer ferritic alloy by composite electrodeposition

Mn 1.4 Co 1.4 Cu 0.2 O 4 spinel protective coating on ferritic stainless steels for solid oxide fuel cell interconnect applications

Cu- and Ce-doped MnCo2O4 Spinel Coatings on Ferrite Interconnects by Electrophoretic Deposition

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

Highly dense (Mn,Co)3O4 spinel protective coating derived from Mn–Co metal precursors for SOFC interconnect applications

Oxidation behavior of Cu-doped MnCo 2 O 4 spinel coating on ferritic stainless steels for solid oxide fuel cell interconnects

Fabrication Of Mn-Co Spinel Coatings On Crofer 22 Apu Stainless Steel By Electrophoretic Deposition For Interconnect Applications In Solid Oxide Fuel Cells

Review—(Mn,Co)3O4-Based Spinels for SOFC Interconnect Coating Application

Influences of Composite Electrodeposition Parameters on the Properties of Ni-Doped Co-Mn Composite Spinel Coatings

CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels as efficient protective coating layers on SUS430 for SOFC interconnect

Highly Conductive Mn-Co Spinel Powder Prepared by Cu-Doping Used for Interconnect Protection of SOFC

Investigation of MnCu0.5Co1.5O4 spinel coated SUS430 interconnect alloy for preventing chromium vaporization in intermediate temperature solid oxide fuel cell

Cu-Fe spinel coating as oxidation barrier for Fe-16Cr metallic interconnect in solid oxide fuel cells

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Comparison of iron and copper doped manganese cobalt spinel oxides as protective coatings for solid oxide fuel cell interconnects

Cufe2o4 Nano-Spherical Powder Directly Served As Interconnect Coating for Solid Oxide Fuel Cells Applications

Transition Metal Spinel Oxide Coatings for Reducing Chromium Poisoning in SOFCs

Iron doped manganese cobaltite spinel coatings produced by electrophoretic co-deposition on interconnects for solid oxide cells: Microstructural and electrical characterization

Synthesis and characterization of nanostructured Cux (Mn1.5-x/2Co1.5-x/2)O4 as an interconnect coating for solid oxide fuel cell

Fabricating a MnCo coating to improve oxidation resistance and electrical conductivity of Crofer22H alloy as SOFC interconnect

Oxidation of MnCu0.5Co1.5O4 Spinel Coated SUS430 Alloy Interconnect in Anode and Cathode Atmospheres for Intermediate Temperature Solid Oxide Fuel Cell