Abstract:In this study, CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels are examined as protective coatings for chromium diffusion in metallic interconnect of solid oxide fuel cell. Both spinels are prepared by co-precipitation technique in order to obtain high temperature conducting spinels. The spinels obtained after 4 h of calcinations in air at 500 °C exhibit tetragonal crystal structure with average grain size between 90 and 100 nm. Cu0.5Co0.5Mn2O4 spinel exhibits superior electrical conductivity over CoMn2O4 and both display NTCR (negative temperature co-efficient of resistance) behavior illustrating their use as a protective layer on interconnects for fuel cells operating at higher temperatures. Doctor-blade employed spinel coating over SUS430 alloy exhibits good adhesion between protective spinel layer and metallic alloy. Cross section micrographs reveal presence of nanosized and highly dense grains capable to resist the outflow of chromium ions present in SUS430. Mass gain and diffusion rate constant (Kp) was high for CoMn2O4 coated SUS430 illustrating Cu0.5Co0.5Mn2O4 spinel as a better protective coating layer for interconnect application. Chromium outflow is restricted and the same is evident from all cross-section micrographs of spinel coated SUS430 specimens subjected for oxidation up to 1000 h. Estimated thickness of Cr2O3 layer was ∼15 nm for CoMn2O4 whereas Cu0.5Co0.5Mn2O4 coated SUS430 specimen had ∼12.5 μm thickness at the SUS430/spinel interface demonstrating superior resistance to chromium outflow. The area specific resistance was lowest for Cu0.5Co0.5Mn2O4 coated specimen (between 14 mΩcm2 – 15 mΩcm2) followed by CoMn2O4 coated specimen reiterating Cu0.5Co0.5Mn2O4 as efficient protective coating material for SUS430 SOFC interconnect.

Thermal Growth and Performance of Manganese Cobaltite Spinel Protection Layers on Ferritic Stainless Steel SOFC Interconnects

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

Research Progresses in the Preparation of Spinel Coatings on the Surface of SOFC Ferrite Stainless Steel Interconnectors

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Review—(Mn,Co)3O4-Based Spinels for SOFC Interconnect Coating Application

CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels as efficient protective coating layers on SUS430 for SOFC interconnect

Mn–Co spinel protective–conductive coating on AL453 ferritic stainless steel for IT-SOFC interconnect applications

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Highly dense (Mn,Co)3O4 spinel protective coating derived from Mn–Co metal precursors for SOFC interconnect applications

Influences of Composite Electrodeposition Parameters on the Properties of Ni-Doped Co-Mn Composite Spinel Coatings

Mechanical reliability and life prediction of coated metallic interconnects within solid oxide fuel cells

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Performance and In-Situ Densification of Mn-Co Spinel Coating on SUS430/441 Interconnect by Spraying Method

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

Iron doped manganese cobaltite spinel coatings produced by electrophoretic co-deposition on interconnects for solid oxide cells: Microstructural and electrical characterization

Evaluation of the Reactive-Sintered (mn,co)3o4 Spinel Layer for SOFC Cathode-Side Contact Application

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

High Temperature Oxidation Behavior of SUS430 SOFC Interconnects with Mn-Co Spinel Coating in Air

Investigation of high‐entropy alloy derived spinel‐based layer for SOFC cathode‐side contact application

Cu and Y doped (Co, Mn)3O4 spinel coatings on Crofer ferritic alloy by composite electrodeposition