Abstract:The effects of the powder size distribution on the hot deformation behavior and the microstructural differences of a novel nickel-based powder metallurgy superalloy (WZ-A3) were studied by SEM, EDS, EBSD, OM, and the thermal simulation testing machine. The results show that compared with HIP-01 sample made from fine powder, the dendrite structure of coarse powder is obvious and the composition segregation is serious. The residual primary gamma' of the HIP-02 sample made from the coarse powder is more than that of the HIP-01 sample. At the low temperature (1050, 1080 degrees C) and high strain rates (1, 0.1 s(-1)), the peak stress of HIP-01 sample is higher than that of HIP-02 sample. After hot compression, the crack situation at the edge of HIP-01 sample is more severe than that of HIP-02 sample. Most of the original microstructure of HIP-01 sample are retained, and the crack is generated at the prior particle boundary (PPB), while some recrystallized structure appears at the edge of HIP-02 sample. At 1080 degrees C/0.001 s(-1), the peak stress of HIP-02 sample is about 30 MPa lower than that of HIP-01 sample. The recrystallization phenomenon of HIP-02 sample during hot compression is obvious and the recrystallized grains are uniform. The HIP-01 has necklace crystal structure, and the recrystallization is not sufficient. The coarse gamma' can promote the recrystallization of HIP-02 sample at 1050 and 1080 degrees C. At high temperature (1150 degrees C) and low strain rates (0.001, 0.01 s(-1)), the gamma' dissolve into. matrix, and the thermal deformation behavior of the two samples is similar. No cracks occur in the samples, and the microstructure is fully recrystallized. The abnormal grown grains are found in the both samples at 1150 degrees C/0.001 s(-1).

Effect of Long-Term Aging on Microstructure Stability of a Novel Nickel Base Powder Superalloy

The Effect of Al on Microstructure and Properties of Cu-15Ni-8Sn During the Aging

Influence of Cooling Rate on the Formation of Bimodal Microstructures in Nickel-Base Superalloys During Continuous Two-Step Aging

The Effect of Long-Term Aging on the Microstructure and Properties of a Novel Nickel-Based Powder Superalloy FGH4113A

Correlations Between Microstructure Evolution and Mechanical Behavior of a Nickel-Based Single Crystal Superalloy with Long-Term Aging Effects

Impact of Aging Temperature on the Performance of a Nickel-Iron-Based Superalloy

Microstructural Evolution and Hardness of a Heat Resistant Alloy During Long Term Aging at 700 °C

Investigation on γ′ stability in CoNi-based superalloys during long-term aging at 900 °C

Study of Aging Temperature on the Thermal Compression Behaviors and Microstructure of a Novel Ni-Cr-Co-Based Superalloy

Order phase transition of HIP nickel-based powder superalloy during isothermal aging

Microstructural Stability of Long-Term Aged Wrought Ni–Fe-based Superalloys

Microstructure evolution of a nickel‐based powder metallurgy superalloy under different solution treatment temperatures

Evolution of microstructure and δ phase in an aging-treated nickel-based superalloy during hot compression

Effect of Heat Treatment on the Microstructure and Fracture Behaviors of a Ni–Cr–Fe Superalloy

Gamma Prime Precipitate Evolution During Aging of a Model Nickel-Based Superalloy

Coarsening kinetics of γ′ phase in isothermal aged high Al content Ni–17 at.% Al alloy

Precipitation behaviors of the rapidly-solidified Allvac 718Plus superalloy during aging treatment

Effect of the Powder Size Distribution on the Hot Deformation Behavior of a Novel Nickel-based Powder Metallurgy Superalloy

Investigation of Precipitation Behavior of a Novel Ni-Fe-Based Superalloy during High-Temperature Aging Treatment

Precipitation behavior of γ′ phase with a multi-model morphology in the Ni-based superalloy GH4720Li during water quenching and subsequent artificial aging and related mechanisms

Effect of Microstructural Evolution and Mechanical Properties of Haynes 230 Superalloy During Long-Term Aging at 700 °C