Effect of Solid Loading of Slurry on Properties of Si₃N₄ Ceramics Formed by Digital Light Processing

Li Meng,Huang Hailu,Wu Jiamin,Liu Chunlei,Wu Yaru,Zhang Jingxian,Shi Yusheng

DOI: https://doi.org/10.15541/jim20210609

IF: 1.292

2022-01-01

Journal of Inorganic Materials

Abstract:With the continuous development of science and technology, Si3N4 ceramics are playing an increasingly important role in high-tech fields such as aviation machinery, biology and medical treatment. In this work, Si3N4 ceramics were successfully prepared by digital light processing (DLP) technology using Si3N4 powder coated with Al2O3-Y2O3 as raw material. Effects of solid loading of slurry on the performance of Si3N4 ceramic slurry, Si3N4 ceramic green parts and Si3N4 ceramics were systematically studied. The results showed that when the solid loading of slurry was less than 40.0% (in volume), its viscosity was less than 2 Pa.s at shear rate of 30 s(-1), which can be used for DLP forming. In that case, the single curing depth of the slurry decreased with the increase of solid loading of the slurry, while the relative density and flexural strength of Si3N4 ceramics formed by DLP increased firstly and then decreased. The relative density and flexural strength reached the maximum of 89.8% and 162.5 MPa at solid loading of 37.5% (in volume), which were 10% and 16% higher than those with solid loading of 32.5% (in volume), respectively. In this work, the properties of Si3N4 ceramics formed by DLP were optimized by determining the best solid loading, which laid the experimental foundation for the photocuring of non-oxide ceramics such as Si3N4.