Achieving the synergy of low thermal conductivity and superior mechanical properties of Ce doping La2Zr2O7 ceramics for thermal protection coatings: Experiment and first-principles calculations
Dongyang Zhang,Cheng Yang,Dazhao Liu,Yang Liu,Peng Zhou,Lu Ren,Dongbai Sun
DOI: https://doi.org/10.1016/j.jpcs.2022.110606
IF: 4.383
2022-04-01
Journal of Physics and Chemistry of Solids
Abstract:The bulk La2(Zr0.7Ce0.3)2O7 (LZ7C) ceramics were successfully fabricated by a novel high-temperature pressureless sintering technique using solid sintering synthesized La2(Zr0.7Ce0.3)2O7 powders. The synthesized ceramic powders presented a mixed pyrochlore and fluorite phase with a smooth average grain size of 410 nm, which was benefit to bulk ceramic densification. The relative density of LZ7C sample was enhanced with the increasing sintering temperature, leading to an enhancement in mechanical properties, especially in fracture toughness, from 0.28 ± 0.05 MPa·m1/2 under 1300 °C increased to 1.41 ± 0.20 MPa·m1/2 under 1500 °C. The calculated thermal conductivity based on the Slack's model was approached to 0.467 W/(m·K) at 300K, which was close to the experimental result (0.493 W/(m·K), RT) of LZ7C-1400 sample. The calculated average coefficient of thermal expansion using QHA method was approached to 6.45 × 10−6 K−1, lower than that of experimental result (8.75 × 10−6 K−1) of LZ7C-1400 sample, which was mainly attributed to the defects, pores and grain boundaries in experiment samples.
physics, condensed matter,chemistry, multidisciplinary